Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel /
Thesis (Sarjana Kejuruteraan Mekanikal)) - Universiti Teknologi Malaysia, 2007
Main Authors: | , |
---|---|
Format: | |
Language: | eng |
Published: |
2007
|
Subjects: |
_version_ | 1826438568830042112 |
---|---|
author | Mohamad Haidir Maslan, 1981- Fakulti Kejuruteraan Mekanikal |
author_facet | Mohamad Haidir Maslan, 1981- Fakulti Kejuruteraan Mekanikal |
author_sort | Mohamad Haidir Maslan, 1981- |
collection | OCEAN |
description | Thesis (Sarjana Kejuruteraan Mekanikal)) - Universiti Teknologi Malaysia, 2007 |
first_indexed | 2024-03-05T09:02:14Z |
format | |
id | KOHA-OAI-TEST:410868 |
institution | Universiti Teknologi Malaysia - OCEAN |
language | eng |
last_indexed | 2024-03-05T09:02:14Z |
publishDate | 2007 |
record_format | dspace |
spelling | KOHA-OAI-TEST:4108682020-12-19T17:14:20ZEffects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / Mohamad Haidir Maslan, 1981- Fakulti Kejuruteraan Mekanikal 2007engThesis (Sarjana Kejuruteraan Mekanikal)) - Universiti Teknologi Malaysia, 2007PSZJBLPressure vessels |
spellingShingle | Pressure vessels Mohamad Haidir Maslan, 1981- Fakulti Kejuruteraan Mekanikal Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / |
title | Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / |
title_full | Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / |
title_fullStr | Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / |
title_full_unstemmed | Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / |
title_short | Effects of absorbed hydrogen on fracture toughness of welded SA516 Grade-70 steel / |
title_sort | effects of absorbed hydrogen on fracture toughness of welded sa516 grade 70 steel |
topic | Pressure vessels |
work_keys_str_mv | AT mohamadhaidirmaslan1981 effectsofabsorbedhydrogenonfracturetoughnessofweldedsa516grade70steel AT fakultikejuruteraanmekanikal effectsofabsorbedhydrogenonfracturetoughnessofweldedsa516grade70steel |