Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding
This study focuses on the effect of pin taper tool ratio on friction stir welding of aluminum AA7075. Two pieces of AA7075 alloy with thickness of 6 mm were friction stir welded by using conventional milling machine. The shoulder diameter used in this experiment is fixed at 18mm. The taper pin ra...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Trans Tech Publications, Switzerland
2016
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/14359/1/fkm-2016-hidayah-Effect%20of%20Taper%20Pin%20Ratio%20on%20AA7075.pdf |
| _version_ | 1825823152184229888 |
|---|---|
| author | Nurul Hidayah, Othman Norsyahfiana, Abdul Razak L. H., Shah M., Ishak |
| author_facet | Nurul Hidayah, Othman Norsyahfiana, Abdul Razak L. H., Shah M., Ishak |
| author_sort | Nurul Hidayah, Othman |
| collection | UMP |
| description | This study focuses on the effect of pin taper tool ratio on friction stir welding of
aluminum AA7075. Two pieces of AA7075 alloy with thickness of 6 mm were friction stir welded
by using conventional milling machine. The shoulder diameter used in this experiment is fixed at
18mm. The taper pin ratio used are varied at 6:6, 6:5, 6:4, 6:3, 6:2 and 6:1. The rotational speeds
that were used in this study were 1000 rpm, 1200 rpm and 1400 rpm, respectively. The welding
speeds used are 60 mm/min, 80 mm/min and 100 mm/min. Microstructure observation of welded
area was studied by using optical microscope. To evaluate the mechanical properties of this
specimen, tensile test was used in this study. Welded specimens using taper pin ratio 6:2 shows
higher tensile strength compared to other taper pin ratio up to 197 MPa. Moreover, specimens using
taper pin ratio 6:1 showed better tensile test compared to the ones using taper pin ratio above 6:3.
The optimum parameters were found to be taper pin ratio 6:2 with 1000 rpm of rotational speed and
60mm/min welding speed |
| first_indexed | 2024-03-06T12:07:08Z |
| format | Article |
| id | UMPir14359 |
| institution | Universiti Malaysia Pahang |
| language | English |
| last_indexed | 2024-03-06T12:07:08Z |
| publishDate | 2016 |
| publisher | Trans Tech Publications, Switzerland |
| record_format | dspace |
| spelling | UMPir143592016-09-21T04:23:34Z http://umpir.ump.edu.my/id/eprint/14359/ Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding Nurul Hidayah, Othman Norsyahfiana, Abdul Razak L. H., Shah M., Ishak TJ Mechanical engineering and machinery This study focuses on the effect of pin taper tool ratio on friction stir welding of aluminum AA7075. Two pieces of AA7075 alloy with thickness of 6 mm were friction stir welded by using conventional milling machine. The shoulder diameter used in this experiment is fixed at 18mm. The taper pin ratio used are varied at 6:6, 6:5, 6:4, 6:3, 6:2 and 6:1. The rotational speeds that were used in this study were 1000 rpm, 1200 rpm and 1400 rpm, respectively. The welding speeds used are 60 mm/min, 80 mm/min and 100 mm/min. Microstructure observation of welded area was studied by using optical microscope. To evaluate the mechanical properties of this specimen, tensile test was used in this study. Welded specimens using taper pin ratio 6:2 shows higher tensile strength compared to other taper pin ratio up to 197 MPa. Moreover, specimens using taper pin ratio 6:1 showed better tensile test compared to the ones using taper pin ratio above 6:3. The optimum parameters were found to be taper pin ratio 6:2 with 1000 rpm of rotational speed and 60mm/min welding speed Trans Tech Publications, Switzerland 2016 Article PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/14359/1/fkm-2016-hidayah-Effect%20of%20Taper%20Pin%20Ratio%20on%20AA7075.pdf Nurul Hidayah, Othman and Norsyahfiana, Abdul Razak and L. H., Shah and M., Ishak (2016) Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding. Key Engineering Materials, 701. pp. 154-158. ISSN 1013-9826 (print); 1662-9795 (online). (Published) http://www.scientific.net/KEM.701.154 DOI: 10.4028/www.scientific.net/KEM.701.154 |
| spellingShingle | TJ Mechanical engineering and machinery Nurul Hidayah, Othman Norsyahfiana, Abdul Razak L. H., Shah M., Ishak Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding |
| title | Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding |
| title_full | Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding |
| title_fullStr | Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding |
| title_full_unstemmed | Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding |
| title_short | Effect of Taper Pin Ratio on AA7075 Aluminium Alloy Friction Stir Welding |
| title_sort | effect of taper pin ratio on aa7075 aluminium alloy friction stir welding |
| topic | TJ Mechanical engineering and machinery |
| url | http://umpir.ump.edu.my/id/eprint/14359/1/fkm-2016-hidayah-Effect%20of%20Taper%20Pin%20Ratio%20on%20AA7075.pdf |
| work_keys_str_mv | AT nurulhidayahothman effectoftaperpinratioonaa7075aluminiumalloyfrictionstirwelding AT norsyahfianaabdulrazak effectoftaperpinratioonaa7075aluminiumalloyfrictionstirwelding AT lhshah effectoftaperpinratioonaa7075aluminiumalloyfrictionstirwelding AT mishak effectoftaperpinratioonaa7075aluminiumalloyfrictionstirwelding |