The Effects of Different Calcination Parameters on CCTO Formation
Dielectric material CaCu3Ti4O12 (CCTO) was prepared by solid state technique. CaCO3, TiO2 and CuO powders were mixed thoroughly in a ball mill for an hour. The mixed powder was calcined at 800 and 900oC for different durations. The calcined samples were subjected to XRD phase analysis and SEM obse...
| Main Authors: | , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2008
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/1523/1/The_Effects_of_Different_Calcination_Parameters_on_CCTO_Formation.pdf |
| _version_ | 1825821135377268736 |
|---|---|
| author | Julie J., Mohamed M. M., Noor |
| author_facet | Julie J., Mohamed M. M., Noor |
| author_sort | Julie J., Mohamed |
| collection | UMP |
| description | Dielectric material CaCu3Ti4O12 (CCTO) was prepared by solid state technique. CaCO3, TiO2 and CuO powders
were mixed thoroughly in a ball mill for an hour. The mixed powder was calcined at 800 and 900oC for different durations. The calcined samples were subjected to XRD phase analysis and SEM observation. All the samples were sintered at 1050 oC for 24 hours, before dielectric constant measurement was done. The effects of different calcination parameters on phase formation, microstructures, and dielectric constant were reported. XRD results show the different phase formations, and the CCTO single phase was first detected for the sample calcined at 900 oC for 6 hours. Increasing the temperature and duration enhances the density, dielectric constant value and the grain growth was observed. The CCTO single phase with the highest dielectric
constant was obtained by calcination at 900oC for 12 hours. |
| first_indexed | 2024-03-06T11:36:58Z |
| format | Conference or Workshop Item |
| id | UMPir1523 |
| institution | Universiti Malaysia Pahang |
| language | English |
| last_indexed | 2024-03-06T11:36:58Z |
| publishDate | 2008 |
| record_format | dspace |
| spelling | UMPir15232016-05-10T03:26:07Z http://umpir.ump.edu.my/id/eprint/1523/ The Effects of Different Calcination Parameters on CCTO Formation Julie J., Mohamed M. M., Noor TJ Mechanical engineering and machinery Dielectric material CaCu3Ti4O12 (CCTO) was prepared by solid state technique. CaCO3, TiO2 and CuO powders were mixed thoroughly in a ball mill for an hour. The mixed powder was calcined at 800 and 900oC for different durations. The calcined samples were subjected to XRD phase analysis and SEM observation. All the samples were sintered at 1050 oC for 24 hours, before dielectric constant measurement was done. The effects of different calcination parameters on phase formation, microstructures, and dielectric constant were reported. XRD results show the different phase formations, and the CCTO single phase was first detected for the sample calcined at 900 oC for 6 hours. Increasing the temperature and duration enhances the density, dielectric constant value and the grain growth was observed. The CCTO single phase with the highest dielectric constant was obtained by calcination at 900oC for 12 hours. 2008 Conference or Workshop Item PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/1523/1/The_Effects_of_Different_Calcination_Parameters_on_CCTO_Formation.pdf Julie J., Mohamed and M. M., Noor (2008) The Effects of Different Calcination Parameters on CCTO Formation. In: Proceeding of Malaysian Technical Universities Conference on Engineering and Technology (MUCET 2008) , March 8-10 2008 , Putra Palace, Perlis, Malaysia. pp. 336-340.. (Published) |
| spellingShingle | TJ Mechanical engineering and machinery Julie J., Mohamed M. M., Noor The Effects of Different Calcination Parameters on CCTO Formation |
| title | The Effects of Different Calcination Parameters on CCTO Formation |
| title_full | The Effects of Different Calcination Parameters on CCTO Formation |
| title_fullStr | The Effects of Different Calcination Parameters on CCTO Formation |
| title_full_unstemmed | The Effects of Different Calcination Parameters on CCTO Formation |
| title_short | The Effects of Different Calcination Parameters on CCTO Formation |
| title_sort | effects of different calcination parameters on ccto formation |
| topic | TJ Mechanical engineering and machinery |
| url | http://umpir.ump.edu.my/id/eprint/1523/1/The_Effects_of_Different_Calcination_Parameters_on_CCTO_Formation.pdf |
| work_keys_str_mv | AT juliejmohamed theeffectsofdifferentcalcinationparametersoncctoformation AT mmnoor theeffectsofdifferentcalcinationparametersoncctoformation AT juliejmohamed effectsofdifferentcalcinationparametersoncctoformation AT mmnoor effectsofdifferentcalcinationparametersoncctoformation |