Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/ TiN experienced severe intergr...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2010
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/2248/1/Aspects_of_Wear_Mechanisms_of_Carbide_Tools_when_Machine.pdf |
| _version_ | 1825821234155225088 |
|---|---|
| author | K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb |
| author_facet | K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb |
| author_sort | K., Kadirgama |
| collection | UMP |
| description | In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/ TiN experienced severe intergranular fractures and cracks. High temperature causes the layer of the coating to wear off and subsequently the inserts damaged at fast rates. Both types of inserts suffered from high crater wear and thermal cracking. Most of the wear occurred at the nose and flank of the inserts. Generally, it was observed that carbide coated with TiALN/ TiN cutting tool performed better than carbide coated TiCN/TiN cutting tool when milling Hastelloy C-22HS |
| first_indexed | 2024-03-06T11:38:27Z |
| format | Article |
| id | UMPir2248 |
| institution | Universiti Malaysia Pahang |
| language | English |
| last_indexed | 2024-03-06T11:38:27Z |
| publishDate | 2010 |
| record_format | dspace |
| spelling | UMPir22482018-01-31T00:55:37Z http://umpir.ump.edu.my/id/eprint/2248/ Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb TJ Mechanical engineering and machinery In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/ TiN experienced severe intergranular fractures and cracks. High temperature causes the layer of the coating to wear off and subsequently the inserts damaged at fast rates. Both types of inserts suffered from high crater wear and thermal cracking. Most of the wear occurred at the nose and flank of the inserts. Generally, it was observed that carbide coated with TiALN/ TiN cutting tool performed better than carbide coated TiCN/TiN cutting tool when milling Hastelloy C-22HS 2010 Article PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/2248/1/Aspects_of_Wear_Mechanisms_of_Carbide_Tools_when_Machine.pdf K., Kadirgama and M. M., Noor and B., Mohammad and H. H., Habeeb (2010) Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS. Advanced Materials Research, 83-86 . pp. 295-302. ISSN 1022-6680. (Published) http://www.scientific.net/AMR.83-86.295 |
| spellingShingle | TJ Mechanical engineering and machinery K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS |
| title | Aspects of Wear Mechanisms of Carbide Tools when Machine
Hastelloy C-22HS
|
| title_full | Aspects of Wear Mechanisms of Carbide Tools when Machine
Hastelloy C-22HS
|
| title_fullStr | Aspects of Wear Mechanisms of Carbide Tools when Machine
Hastelloy C-22HS
|
| title_full_unstemmed | Aspects of Wear Mechanisms of Carbide Tools when Machine
Hastelloy C-22HS
|
| title_short | Aspects of Wear Mechanisms of Carbide Tools when Machine
Hastelloy C-22HS
|
| title_sort | aspects of wear mechanisms of carbide tools when machine hastelloy c 22hs |
| topic | TJ Mechanical engineering and machinery |
| url | http://umpir.ump.edu.my/id/eprint/2248/1/Aspects_of_Wear_Mechanisms_of_Carbide_Tools_when_Machine.pdf |
| work_keys_str_mv | AT kkadirgama aspectsofwearmechanismsofcarbidetoolswhenmachinehastelloyc22hs AT mmnoor aspectsofwearmechanismsofcarbidetoolswhenmachinehastelloyc22hs AT bmohammad aspectsofwearmechanismsofcarbidetoolswhenmachinehastelloyc22hs AT hhhabeeb aspectsofwearmechanismsofcarbidetoolswhenmachinehastelloyc22hs |