In-vitro biocompatibility study of hydroxyapatite coated on Co-Cr-Mo with oxide interlayer

In-vitro biocompatibility study of hydroxyapatite coated on Co-Cr-Mo with oxide interlayer

Hiển thị phiên bản (1) khác

The effects of oxide interlayer on cobalt-chromium-molybdenum substrate were investigated in order to improve the quality of hydroxyapatite (HA) coating as well as enhance the cell responses. Substrates were oxidized at temperature of 850 °C and 1050 °C for 3 hours. Oxidized substrates were then coa...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Mas Ayu, Hassan, R., Daud, Sudin, Izman, Arman Shah, Abdullah, Mahmood, Anwar, Krishnamurithy, G., Tunku, Kamarul
Định dạng:	Bài viết
Ngôn ngữ:	English
Được phát hành:	Penerbit Universiti Teknologi Malaysia 2018
Những chủ đề:	TJ Mechanical engineering and machinery
Truy cập trực tuyến:	http://umpir.ump.edu.my/id/eprint/24040/1/In-vitro%20biocompatibility%20study%20of%20hydroxyapatite%20coated%20on%20Co-Cr-Mo%20with%20oxide%20interlayer.pdf

Những quyển sách tương tự

In-vitro biocompatibility study of hydroxyapatite coated on Co-Cr-Mo with oxide interlayer
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2017)

Effects of hydroxyapatite coating with oxide interlayer on bioactivity performances in CoCrMo alloy /
Bằng: Mas Ayu Hassan, 1982-, author, et al.
Được phát hành: (2015)

Creating Oxide Interlayer Through Thermal Oxidation Improves Adhesion Strength Of Hydroxyapatite Coating on Co-Cr-Mo Substrates
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2015)

Effects of hydroxyapatite coating with oxide interlayer on bioactivity performances in CoCrMo alloy
Bằng: Mas Ayu, Hassan
Được phát hành: (2015)

Surface Modification on CoCrMo Alloy to Improve the Adhesion Strength of Hydroxyapatite Coating
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2017)

Effects of hydroxyapatite coating with oxide interlayer on bioactivity performances in CoCrMo alloy [electronic resource] /
Bằng: Mas Ayu Hassan, 1982-, author
Được phát hành: (2015)

The Effects of Oxide Layer on Co-Cr-Mo: Preliminary Study In-vitro
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2015)

Effect of biodegradable PLA on hydroxyapatite coating to improve adhesion properties on Cr-Co-Mo alloy
Bằng: Mas Ayu, H.
Được phát hành: (2020)

Hydroxyapatite coating with oxide interlayer on biomedical grade cobalt based alloy
Bằng: Mas Ayu, H.
Được phát hành: (2017)

A study of hydroxyapatite coating for biocompatible materials /
Bằng: Atefeh Ayatollah Tafti, 1980-, author 638914, et al.
Được phát hành: (2016)

Biocompatibility of Gentamicin-coated Hydroxyapatite (Ha) with osteoblast.
Bằng: Othman, Fauziah, et al.
Được phát hành: (2010)

Improving biocompatibility of cobalt based alloy using chemical etching and mechanical treatment
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2018)

Thermal oxidation promotes growth of nanocrystalline diamond on biomedical grade Co Cr mo alloy
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2019)

A Review of Hydroxyapatite-Based Coating Techniques: Sol–Gel and Electrochemical Depositions on Biocompatible Metals
Bằng: Rahil Izzati, Mohd Asri, et al.
Được phát hành: (2016)

A study of hydroxyapatite coating for biocompatible materials [electronic resource] /
Bằng: Atefeh Ayatollah Tafti, 1980-, author 638914
Được phát hành: (2016)

Fluorescence microscopy on the biocompatibility of gentamicin-coated hydroxyapatite (HA) material on osteoblast
Bằng: Che Seman, Che Nor Zarida, et al.
Được phát hành: (2010)

In-vitro bioactivity, biocompatibility and dissolution studies of diopside prepared from biowaste by using sol–gel combustion method
Bằng: Choudhary, R., et al.
Được phát hành: (2016)

Effect of pickling temperature on adhesion strength of Ti oxide interlayer prior to diamond coating /
Bằng: Khor, Eng Kean, 1986-, et al.
Được phát hành: (2010)

Effect of pickling time on adhesion strength of ti oxide interlayer prior to diamond coating /
Bằng: Low, Yik Kuan, 1986-, et al.
Được phát hành: (2010)

Study on adhesion strength of tin coated biomedical ti-13zr-13nb alloy
Bằng: Arman Shah, Abdullah, et al.
Được phát hành: (2018)

The Effect of PLA/HA Coating Thickness on Crack Formation and Corrosion Performance
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2022)

Synergized poly(lactic acid)-hydroxyapatite composites: Biocompatibility study
Bằng: Akindoyo, John Olabode, et al.
Được phát hành: (2018)

Biocompatibility of porous hydroxyapatite microcarrier for vero cell culture application
Bằng: Mel, Maizirwan, et al.
Được phát hành: (2011)

Biocompatibility of metal-ion-substituted hydroxyapatite as orthopaedic/dental implant
Bằng: Jasmine Widodo
Được phát hành: (2009)

Antibacterial, biocompatibility and nanomechanical properties of TI-6AL-7NB alloy coated with copper, hydroxyapatite and copper ion doped hydroxyapatite for dental implants
Bằng: Al-Murshedi, Hanan Ali Hameed
Được phát hành: (2018)

Evaluating the surface properties of HA coating on Co-Cr based alloy substrate /
Bằng: Hirbod Maleki Kheimeh Sari, 1986-, et al.
Được phát hành: (2014)

Spectroscopic Signatures of Interlayer Coupling in Janus MoSSe/MoS 2 Heterostructures
Bằng: Zhang, Kunyan, et al.
Được phát hành: (2022)

Deformation Behaviour of a High Carbon Co–Cr–Mo Medium-Entropy Alloy via Thermal Oxidation
Bằng: Rosdi, Daud, et al.
Được phát hành: (2023)

Mechanical, antibacterial, and biocompatibility mechanism of PVD grown silver–tantalum-oxide-based nanostructured thin film on stainless steel 316L for surgical applications
Bằng: Alias, Rodianah, et al.
Được phát hành: (2020)

Effect of Thermal Oxidation and Carbon Concentrations on Co-Cr-Mo Alloy in Enhanced Corrosion Protection
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2018)

Ab initio calculation of the electronic structure of Fe and Cr interlayers
Bằng: Ahmad Zabidi, N., et al.
Được phát hành: (2010)

Effect of thermal oxidation and carbon concentration on Co-Cr-Mo alloy in enhanced corrosion protection
Bằng: Mas Ayu, Hassan, et al.
Được phát hành: (2018)

Effect of carburization process parameters on adhesion strength of titanium carbide interlayer /
Bằng: Adila Nalisa Mohd. Roslan, 1989-, et al.
Được phát hành: (2011)

Dissipated energy and fretting damage in CoCrAlY-MoS₂ coatings
Bằng: Kim, K, et al.
Được phát hành: (2010)

In vitro biocompatibility of diazirine-grafted biomaterials
Bằng: Djordjevic, Ivan, et al.
Được phát hành: (2020)

Effect post treatment parameters on corrosion resistance of Ti-13Nb- 13Zr coated with hydroxyapatite via electrophoretic deposition /
Bằng: Nabeel Najm Bahlol, 1984- author, et al.
Được phát hành: (2015)

Structure and properties of Co‑Cr alloys for biocompatible medical products
Bằng: P. E. Lushchik, et al.
Được phát hành: (2023-01-01)

The effect of hydroxyapatite addition on biocompatibility of porous alumina microcarriers for vero cell culture
Bằng: Fadli, Ahmad, et al.
Được phát hành: (2011)

Characterization of bovine-derived porous hydroxyapatite scaffold and its potential to support osteogenic differentiation of human bone marrow derived mesenchymal stem cells
Bằng: Krishnamurithy, G., et al.
Được phát hành: (2014)

Development of Talus Implant based on Artificial Neural Network prediction of Talus Morphological Parameters
Bằng: R., Daud, et al.
Được phát hành: (2015)