In-vitro biocompatibility study of hydroxyapatite coated on Co-Cr-Mo with oxide interlayer
The effects of oxide interlayer on cobalt-chromium-molybdenum substrate were investigated in order to improve the quality of hydroxyapatite (HA) coating as well as enhance the cell responses. Substrates were oxidized at temperature of 850 °C and 1050 °C for 3 hours. Oxidized substrates were then coa...
Main Authors: | Mas Ayu, Hassan, R., Daud, Sudin, Izman, Arman Shah, Abdullah, Mahmood, Anwar, Krishnamurithy, G., Tunku, Kamarul |
---|---|
Format: | Article |
Language: | English |
Published: |
Penerbit Universiti Teknologi Malaysia
2018
|
Subjects: | |
Online Access: | http://umpir.ump.edu.my/id/eprint/24040/1/In-vitro%20biocompatibility%20study%20of%20hydroxyapatite%20coated%20on%20Co-Cr-Mo%20with%20oxide%20interlayer.pdf |
Similar Items
-
In-vitro biocompatibility study of hydroxyapatite coated on Co-Cr-Mo with oxide interlayer
by: Mas Ayu, Hassan, et al.
Published: (2017) -
In-vitro biocompatibility study of hydroxyapatite coated on Co-Cr-Mo with oxide interlayer
by: Mas Ayu, H., et al.
Published: (2018) -
Creating Oxide Interlayer Through Thermal Oxidation Improves Adhesion Strength Of Hydroxyapatite Coating on Co-Cr-Mo Substrates
by: Mas Ayu, Hassan, et al.
Published: (2015) -
Surface Modification on CoCrMo Alloy to Improve the Adhesion Strength of Hydroxyapatite Coating
by: Mas Ayu, Hassan, et al.
Published: (2017) -
Effects of hydroxyapatite coating with oxide interlayer on bioactivity performances in CoCrMo alloy
by: Hassan, Mas Ayu
Published: (2015)