The effect of carbon black loadings on tensile strength of rubber vulcanizates
In this study, the effect of filler loadings (carbon black) on the tensile strength of SMR 10 was investigated. The carbon black grade was chosen N220 and the loading ranges were set 20, 40, 50, and 60 parts per hundred rubbers (phr). For the mixing and moulding process, the Two Roll Mill (Model LS-...
| Main Author: | |
|---|---|
| Format: | Undergraduates Project Papers |
| Language: | English |
| Published: |
2010
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/3156/1/CD5890_MOHD_WAQIYUDIN_MOHD_SALEH.pdf |
| _version_ | 1796989649746395136 |
|---|---|
| author | Mohd Waqiyuddin, Mohd Salleh |
| author_facet | Mohd Waqiyuddin, Mohd Salleh |
| author_sort | Mohd Waqiyuddin, Mohd Salleh |
| collection | UMP |
| description | In this study, the effect of filler loadings (carbon black) on the tensile strength of SMR 10 was investigated. The carbon black grade was chosen N220 and the loading ranges were set 20, 40, 50, and 60 parts per hundred rubbers (phr). For the mixing and moulding process, the Two Roll Mill (Model LS-22005) and 25 Ton Hot Cold Molding Press (Model LS22025) was used which is supplied by Lotus Scientific. In order to determine the tensile strength values, a Universal Testing Machine (Model 133004600771) operating at 20 mm/min was used. It was found that the tensile strength increase with the increasing of carbon black loading until it reaches at the maximum interphase interaction between the polymer chains and filler. This observation is attributed to the rubber–filler interphase interaction of carbon black and rubber. |
| first_indexed | 2024-03-06T11:40:13Z |
| format | Undergraduates Project Papers |
| id | UMPir3156 |
| institution | Universiti Malaysia Pahang |
| language | English |
| last_indexed | 2024-03-06T11:40:13Z |
| publishDate | 2010 |
| record_format | dspace |
| spelling | UMPir31562015-04-13T03:16:02Z http://umpir.ump.edu.my/id/eprint/3156/ The effect of carbon black loadings on tensile strength of rubber vulcanizates Mohd Waqiyuddin, Mohd Salleh TP Chemical technology In this study, the effect of filler loadings (carbon black) on the tensile strength of SMR 10 was investigated. The carbon black grade was chosen N220 and the loading ranges were set 20, 40, 50, and 60 parts per hundred rubbers (phr). For the mixing and moulding process, the Two Roll Mill (Model LS-22005) and 25 Ton Hot Cold Molding Press (Model LS22025) was used which is supplied by Lotus Scientific. In order to determine the tensile strength values, a Universal Testing Machine (Model 133004600771) operating at 20 mm/min was used. It was found that the tensile strength increase with the increasing of carbon black loading until it reaches at the maximum interphase interaction between the polymer chains and filler. This observation is attributed to the rubber–filler interphase interaction of carbon black and rubber. 2010-04 Undergraduates Project Papers NonPeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/3156/1/CD5890_MOHD_WAQIYUDIN_MOHD_SALEH.pdf Mohd Waqiyuddin, Mohd Salleh (2010) The effect of carbon black loadings on tensile strength of rubber vulcanizates. Faculty of Chemical & Natural Resources Engineering , Universiti Malaysia Pahang . |
| spellingShingle | TP Chemical technology Mohd Waqiyuddin, Mohd Salleh The effect of carbon black loadings on tensile strength of rubber vulcanizates |
| title | The effect of carbon black loadings on tensile strength of rubber vulcanizates |
| title_full | The effect of carbon black loadings on tensile strength of rubber vulcanizates |
| title_fullStr | The effect of carbon black loadings on tensile strength of rubber vulcanizates |
| title_full_unstemmed | The effect of carbon black loadings on tensile strength of rubber vulcanizates |
| title_short | The effect of carbon black loadings on tensile strength of rubber vulcanizates |
| title_sort | effect of carbon black loadings on tensile strength of rubber vulcanizates |
| topic | TP Chemical technology |
| url | http://umpir.ump.edu.my/id/eprint/3156/1/CD5890_MOHD_WAQIYUDIN_MOHD_SALEH.pdf |
| work_keys_str_mv | AT mohdwaqiyuddinmohdsalleh theeffectofcarbonblackloadingsontensilestrengthofrubbervulcanizates AT mohdwaqiyuddinmohdsalleh effectofcarbonblackloadingsontensilestrengthofrubbervulcanizates |