Synthesis of water-repellent coating for polyester fabric
A new hydrophobic hexyltrimethoxysilane (HTMS) coating for polyester fabric was successfully synthesized via a one-step water-based sol-gel method under acidic condition. Five different molar ratios of HTMS: water (1;40, 1:30, 1:20, 1:12 and 1:3) were prepared and the solution was deposited onto the...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Ital Publication
2021
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/32581/1/Synthesis%20of%20water%20repellent%20coating%20for%20polyester%20fabric.pdf |
| _version_ | 1825814064975052800 |
|---|---|
| author | Nur Nabilah, Mohd Za’im Hartina, Mohd Yusop Wan Norfazilah, Wan Ismail |
| author_facet | Nur Nabilah, Mohd Za’im Hartina, Mohd Yusop Wan Norfazilah, Wan Ismail |
| author_sort | Nur Nabilah, Mohd Za’im |
| collection | UMP |
| description | A new hydrophobic hexyltrimethoxysilane (HTMS) coating for polyester fabric was successfully synthesized via a one-step water-based sol-gel method under acidic condition. Five different molar ratios of HTMS: water (1;40, 1:30, 1:20, 1:12 and 1:3) were prepared and the solution was deposited onto the polyester fabric by a simple dip-pad-cure process. The effect of water content on hydrophobicity was evaluated by manual testing on the treated polyester fabric samples. The effectiveness of hydrophobicity properties was further characterized using water contact angle (WCA) measurement. The optimized molar ratio of 1:3 was found to obtain the best hydrophobic property of 136.2° with particle size 115.3 µm measured using Particle Size Analyzer (PSA). Fourier transform infrared spectroscopy (FTIR) analysis confirmed the success of sol gel process with the presence of Si-O-Si band, which was also determined using energy dispersive X-ray spectroscopy (EDX). The Scanning Electron Microscopy (SEM) images revealed a good surface morphology of the homogenous thin xerogel coating with no visible cracks. Using HTMS without combinations of other precursors resulted in rough surface structure due to the low surface energy caused by long-chain alkyl silane in the HTMS coating and this provided the treated polyester fabric with good hydrophobicity. |
| first_indexed | 2024-03-06T12:53:18Z |
| format | Article |
| id | UMPir32581 |
| institution | Universiti Malaysia Pahang |
| language | English |
| last_indexed | 2024-03-06T12:53:18Z |
| publishDate | 2021 |
| publisher | Ital Publication |
| record_format | dspace |
| spelling | UMPir325812021-11-25T02:59:52Z http://umpir.ump.edu.my/id/eprint/32581/ Synthesis of water-repellent coating for polyester fabric Nur Nabilah, Mohd Za’im Hartina, Mohd Yusop Wan Norfazilah, Wan Ismail TP Chemical technology A new hydrophobic hexyltrimethoxysilane (HTMS) coating for polyester fabric was successfully synthesized via a one-step water-based sol-gel method under acidic condition. Five different molar ratios of HTMS: water (1;40, 1:30, 1:20, 1:12 and 1:3) were prepared and the solution was deposited onto the polyester fabric by a simple dip-pad-cure process. The effect of water content on hydrophobicity was evaluated by manual testing on the treated polyester fabric samples. The effectiveness of hydrophobicity properties was further characterized using water contact angle (WCA) measurement. The optimized molar ratio of 1:3 was found to obtain the best hydrophobic property of 136.2° with particle size 115.3 µm measured using Particle Size Analyzer (PSA). Fourier transform infrared spectroscopy (FTIR) analysis confirmed the success of sol gel process with the presence of Si-O-Si band, which was also determined using energy dispersive X-ray spectroscopy (EDX). The Scanning Electron Microscopy (SEM) images revealed a good surface morphology of the homogenous thin xerogel coating with no visible cracks. Using HTMS without combinations of other precursors resulted in rough surface structure due to the low surface energy caused by long-chain alkyl silane in the HTMS coating and this provided the treated polyester fabric with good hydrophobicity. Ital Publication 2021-10 Article PeerReviewed pdf en cc_by_4 http://umpir.ump.edu.my/id/eprint/32581/1/Synthesis%20of%20water%20repellent%20coating%20for%20polyester%20fabric.pdf Nur Nabilah, Mohd Za’im and Hartina, Mohd Yusop and Wan Norfazilah, Wan Ismail (2021) Synthesis of water-repellent coating for polyester fabric. Emerging Science Journal, 5 (5). 747 -754. ISSN 2610-9182. (Published) http://dx.doi.org/10.28991/esj-2021-01309 http://dx.doi.org/10.28991/esj-2021-01309 |
| spellingShingle | TP Chemical technology Nur Nabilah, Mohd Za’im Hartina, Mohd Yusop Wan Norfazilah, Wan Ismail Synthesis of water-repellent coating for polyester fabric |
| title | Synthesis of water-repellent coating for polyester fabric |
| title_full | Synthesis of water-repellent coating for polyester fabric |
| title_fullStr | Synthesis of water-repellent coating for polyester fabric |
| title_full_unstemmed | Synthesis of water-repellent coating for polyester fabric |
| title_short | Synthesis of water-repellent coating for polyester fabric |
| title_sort | synthesis of water repellent coating for polyester fabric |
| topic | TP Chemical technology |
| url | http://umpir.ump.edu.my/id/eprint/32581/1/Synthesis%20of%20water%20repellent%20coating%20for%20polyester%20fabric.pdf |
| work_keys_str_mv | AT nurnabilahmohdzaim synthesisofwaterrepellentcoatingforpolyesterfabric AT hartinamohdyusop synthesisofwaterrepellentcoatingforpolyesterfabric AT wannorfazilahwanismail synthesisofwaterrepellentcoatingforpolyesterfabric |