Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg)
In this study, Mg-Zn alloys were prepared by using powder metallurgy technique where magnesium (Mg) and zinc (Zn) were regarded as the starting materials. The effect of Zn towards the microstructure and corrosion behaviour of Mg was studied. The microstructure observation, intermetallic particle dis...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier Ltd
2021
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/32680/2/M.A.F.%20Romzi%20a%2C%E2%87%91ArtInPress.pdf |
| _version_ | 1825814084730224640 |
|---|---|
| author | M. A. F., Romzi J., Alias M. I., M. Ramli |
| author_facet | M. A. F., Romzi J., Alias M. I., M. Ramli |
| author_sort | M. A. F., Romzi |
| collection | UMP |
| description | In this study, Mg-Zn alloys were prepared by using powder metallurgy technique where magnesium (Mg) and zinc (Zn) were regarded as the starting materials. The effect of Zn towards the microstructure and corrosion behaviour of Mg was studied. The microstructure observation, intermetallic particle distribution, density and X-ray diffraction (XRD) analysis were measured and studied. Besides, the corrosion behaviour of Mg-Zn alloys was observed from hydrogen evolution test and potentiodynamic polarization test. The results showed that due to the same crystal structure of Mg and Zn which was hexagonal close packed (HCP) structure, MgZn2 was formed and complete solid solubility was achieved. The presence of α-Mg and MgZn2 phases was confirmed from the XRD result. The density of the Mg-Zn alloys was increased as the Zn content increased. From the results, Mg-30Zn has the highest value of density compared to Mg-10Zn and Mg-20Zn due to the Zn particles which filled in the gap between the Mg particles. The corrosion test for Mg-Zn alloys showed that Zn addition does improve the corrosion resistance of Mg alloys. |
| first_indexed | 2024-03-06T12:53:36Z |
| format | Article |
| id | UMPir32680 |
| institution | Universiti Malaysia Pahang |
| language | English |
| last_indexed | 2024-03-06T12:53:36Z |
| publishDate | 2021 |
| publisher | Elsevier Ltd |
| record_format | dspace |
| spelling | UMPir326802021-11-30T07:24:31Z http://umpir.ump.edu.my/id/eprint/32680/ Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) M. A. F., Romzi J., Alias M. I., M. Ramli TJ Mechanical engineering and machinery In this study, Mg-Zn alloys were prepared by using powder metallurgy technique where magnesium (Mg) and zinc (Zn) were regarded as the starting materials. The effect of Zn towards the microstructure and corrosion behaviour of Mg was studied. The microstructure observation, intermetallic particle distribution, density and X-ray diffraction (XRD) analysis were measured and studied. Besides, the corrosion behaviour of Mg-Zn alloys was observed from hydrogen evolution test and potentiodynamic polarization test. The results showed that due to the same crystal structure of Mg and Zn which was hexagonal close packed (HCP) structure, MgZn2 was formed and complete solid solubility was achieved. The presence of α-Mg and MgZn2 phases was confirmed from the XRD result. The density of the Mg-Zn alloys was increased as the Zn content increased. From the results, Mg-30Zn has the highest value of density compared to Mg-10Zn and Mg-20Zn due to the Zn particles which filled in the gap between the Mg particles. The corrosion test for Mg-Zn alloys showed that Zn addition does improve the corrosion resistance of Mg alloys. Elsevier Ltd 2021-10-22 Article NonPeerReviewed pdf en http://umpir.ump.edu.my/id/eprint/32680/2/M.A.F.%20Romzi%20a%2C%E2%87%91ArtInPress.pdf M. A. F., Romzi and J., Alias and M. I., M. Ramli (2021) Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg). Materials Today: Proceedings. pp. 1-7. ISSN 2214-7853. (In Press / Online First) (In Press / Online First) https://www.sciencedirect.com/science/article/pii/S2214785321061204#! : www.elsevier.com/locate/matpr |
| spellingShingle | TJ Mechanical engineering and machinery M. A. F., Romzi J., Alias M. I., M. Ramli Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) |
| title | Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) |
| title_full | Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) |
| title_fullStr | Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) |
| title_full_unstemmed | Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) |
| title_short | Effect of zinc (Zn) on the microstructure and corrosion behaviour of magnesium (Mg) |
| title_sort | effect of zinc zn on the microstructure and corrosion behaviour of magnesium mg |
| topic | TJ Mechanical engineering and machinery |
| url | http://umpir.ump.edu.my/id/eprint/32680/2/M.A.F.%20Romzi%20a%2C%E2%87%91ArtInPress.pdf |
| work_keys_str_mv | AT mafromzi effectofzincznonthemicrostructureandcorrosionbehaviourofmagnesiummg AT jalias effectofzincznonthemicrostructureandcorrosionbehaviourofmagnesiummg AT mimramli effectofzincznonthemicrostructureandcorrosionbehaviourofmagnesiummg |