Tensile properties of alkali treated sugar palm fiber
A study of the effect of alkaline treatment on the tensile properties of sugar palm fiber.The fiber were treated using sodium hydroxide (NaOH) with 2%, 4% and 6% concentration solution for 1 hour soaking time. The purpose of treating fiber with alkali was to enhance the tensile strength and young mo...
| Main Author: | |
|---|---|
| Format: | Undergraduates Project Papers |
| Language: | English English English |
| Published: |
2013
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/8486/1/CD7974_%40_39.pdf http://umpir.ump.edu.my/id/eprint/8486/4/1.pdf http://umpir.ump.edu.my/id/eprint/8486/5/3.pdf |
| _version_ | 1796990449324392448 |
|---|---|
| author | Mohamad Nazirul Mubin, Merzuki |
| author_facet | Mohamad Nazirul Mubin, Merzuki |
| author_sort | Mohamad Nazirul Mubin, Merzuki |
| collection | UMP |
| description | A study of the effect of alkaline treatment on the tensile properties of sugar palm fiber.The fiber were treated using sodium hydroxide (NaOH) with 2%, 4% and 6% concentration solution for 1 hour soaking time. The purpose of treating fiber with alkali was to enhance the tensile strength and young modulus of single sugar palm fiber. The maximum tensile strength for untreated fiber is 63.05 MPa.The maximum tensile strength for occurred at 2% NaOH solution with 1 hour of soaking time, i.e 67.85 MPa. But, the maximum fiber for treated 4% NaOH solution with 1 hour of soaking time is 76.37MPa and for fiber treated 6% NaOH solution is 82.13 MPa. |
| first_indexed | 2024-03-06T11:51:44Z |
| format | Undergraduates Project Papers |
| id | UMPir8486 |
| institution | Universiti Malaysia Pahang |
| language | English English English |
| last_indexed | 2024-03-06T11:51:44Z |
| publishDate | 2013 |
| record_format | dspace |
| spelling | UMPir84862021-06-29T03:23:27Z http://umpir.ump.edu.my/id/eprint/8486/ Tensile properties of alkali treated sugar palm fiber Mohamad Nazirul Mubin, Merzuki TA Engineering (General). Civil engineering (General) A study of the effect of alkaline treatment on the tensile properties of sugar palm fiber.The fiber were treated using sodium hydroxide (NaOH) with 2%, 4% and 6% concentration solution for 1 hour soaking time. The purpose of treating fiber with alkali was to enhance the tensile strength and young modulus of single sugar palm fiber. The maximum tensile strength for untreated fiber is 63.05 MPa.The maximum tensile strength for occurred at 2% NaOH solution with 1 hour of soaking time, i.e 67.85 MPa. But, the maximum fiber for treated 4% NaOH solution with 1 hour of soaking time is 76.37MPa and for fiber treated 6% NaOH solution is 82.13 MPa. 2013-06 Undergraduates Project Papers NonPeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/8486/1/CD7974_%40_39.pdf application/pdf en http://umpir.ump.edu.my/id/eprint/8486/4/1.pdf application/pdf en http://umpir.ump.edu.my/id/eprint/8486/5/3.pdf Mohamad Nazirul Mubin, Merzuki (2013) Tensile properties of alkali treated sugar palm fiber. Faculty of Mechanical Engineering , Universiti Malaysia Pahang. |
| spellingShingle | TA Engineering (General). Civil engineering (General) Mohamad Nazirul Mubin, Merzuki Tensile properties of alkali treated sugar palm fiber |
| title | Tensile properties of alkali treated sugar palm fiber |
| title_full | Tensile properties of alkali treated sugar palm fiber |
| title_fullStr | Tensile properties of alkali treated sugar palm fiber |
| title_full_unstemmed | Tensile properties of alkali treated sugar palm fiber |
| title_short | Tensile properties of alkali treated sugar palm fiber |
| title_sort | tensile properties of alkali treated sugar palm fiber |
| topic | TA Engineering (General). Civil engineering (General) |
| url | http://umpir.ump.edu.my/id/eprint/8486/1/CD7974_%40_39.pdf http://umpir.ump.edu.my/id/eprint/8486/4/1.pdf http://umpir.ump.edu.my/id/eprint/8486/5/3.pdf |
| work_keys_str_mv | AT mohamadnazirulmubinmerzuki tensilepropertiesofalkalitreatedsugarpalmfiber |