The stabilities of microstructures and hardness of P92 steel samples austenitized at 1060℃ for 1h followed by air cooling (AC)/slow cooling (SC) and tempered at 760℃ for 2h and then aged at 650℃ for 1000h/3000h were studied by SEM-SE/BSE,EDS and multiphase separation technology (MPST). The results s...
Main Authors: | ZHONG Jiao, PENG Zhi-fang, CHEN Fang-yu, PENG Fang-fang, LIU Sheng, SHI Zhen-bin |
---|---|
Format: | Article |
Language: | zho |
Published: |
Journal of Materials Engineering
2019-01-01
|
Series: | Cailiao gongcheng |
Subjects: | |
Online Access: | http://jme.biam.ac.cn/CN/Y2019/V47/I1/119 |
Similar Items
-
Phase parameter changes of specific positions of P92 steel specimens during creep rupture test at 625℃
by: LIU Cheng, et al.
Published: (2020-03-01) -
Phase parameter changes of specific positions of P92 steel specimens during creep rupture test at 625℃
by: LIU Cheng, et al.
Published: (2019-03-01) -
INFLUENCE OF COOLING RATE ON THE OCORRENCE OF RETAINED AUSTENITE IN A STEEL FOR WELDING ELECTRODES
by: Helder Carvalho Ferreira, et al.
Published: (2015-07-01) -
Studies on the Oxidation Behavior and Microstructural Evolution of Two Nb-Modified HR3C Austenitic Steels under Pure Water Vapor at 650 °C
by: Jinlong Wang, et al.
Published: (2020-11-01) -
Study of Residual Stresses and Austenite Gradients in the Surface after Hard Turning as a Function of Flank Wear and Cutting Speed
by: Anna Mičietová, et al.
Published: (2023-02-01)