Effect of Non-Isothermal Aging on the Mechanical Properties and Corrosion Resistance of 2A12 Aluminum Alloy
The effect of linear non-isothermal aging and composite non-isothermal aging on the mechanical properties and corrosion resistance of 2A12 aluminum alloy was investigated. Optical microscopy (OM) and scanning electron microscopy (SEM) equipped with energy-dispersive spectroscopy (EDS) were used to s...
Main Authors: | , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-05-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/16/11/3921 |
Summary: | The effect of linear non-isothermal aging and composite non-isothermal aging on the mechanical properties and corrosion resistance of 2A12 aluminum alloy was investigated. Optical microscopy (OM) and scanning electron microscopy (SEM) equipped with energy-dispersive spectroscopy (EDS) were used to study the microstructure and intergranular corrosion morphology, and the precipitates were analyzed using X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results showed that the mechanical properties of 2A12 aluminum alloy were improved by both non-isothermal aging techniques due to the formation of an S′ phase and a point S″ phase in the alloy matrix. Linear non-isothermal aging resulted in better mechanical properties than composite non-isothermal aging. However, the corrosion resistance of the 2A12 aluminum alloy was reduced after non-isothermal aging due to the transformation of matrix precipitates and grain boundary precipitates. The corrosion resistance of the samples followed the order: annealed state > linear non-isothermal aging > composite non-isothermal aging. |
---|---|
ISSN: | 1996-1944 |