Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta
The aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized clas...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of São Paulo
2005-06-01
|
| Series: | Journal of Applied Oral Science |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572005000200019 |
| _version_ | 1817993454882390016 |
|---|---|
| author | Maria Jacinta M. Coelho Santos Mário Honorato da Silva e Souza Júnior Gildo Coelho Santos Júnior Omar El-Mowafy Ana Paula Chedid Cavalcanti Carla Farah Neme |
| author_facet | Maria Jacinta M. Coelho Santos Mário Honorato da Silva e Souza Júnior Gildo Coelho Santos Júnior Omar El-Mowafy Ana Paula Chedid Cavalcanti Carla Farah Neme |
| author_sort | Maria Jacinta M. Coelho Santos |
| collection | DOAJ |
| description | The aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized class V cavities in all dentin margins. Teeth were divided into 5 equal groups according to the curing cycle. The cavities were incrementally restored with a composite resin (Single Bond/Z-100, 3M). Light curing was applied as follows: Group I: PAC light continuous-cycle curing at 1600 mW/cm² for 3s; Group II: PAC light step-cycle curing (2s at 800 mW/cm² then 4s at 1600 mW/cm²); Group III: QTH light continuous-cycle curing at 400 mW/cm² for 40s; Group IV: QTH light ramp-cycle curing (from 100 to 600 mW/cm² in 15s followed by 25s at 600 mW/cm²); Group V: QTH light pulse-delay curing (200 mW/cm² for 3s followed by 3 min delay then 600 mW/cm² for 30s). Teeth were stored in distilled water at 37ºC for 30 days and then subjected to thermocycling for 500 cycles at 5 and 55ºC. Root apices were sealed and teeth coated with nail varnish before they were immersed in 0.5% fuchsine red dye solution. Teeth were then sectioned and slices were scanned with a computer scanner to determine the area of dye leakage using a computer program (Image Tools). Images of tooth slices were also visually examined under magnification and dye penetration along the tooth/restoration interface was scored. Significant differences in the degree of dye penetration and leakage were detected between groups (p<.05). Groups I and II had significantly higher values of dye penetration and leakage than groups III, IV and V. In conclusion, the use of PAC light curing in a continuous or step cycle modes resulted in increased microleakage of Class V resin composite restorations compared with medium intensity QTH light curing. Pulse, ramp and continuous-cycle curing modes with QTH light resulted in similar degrees of microleakage.<br>O objetivo deste estudo foi determinar o efeito da polimerização gradual, mediante a utilização de aparelhos de Quartzo-Tungustênio-Halógena (QTH) e Arco de Plasma de Xenônio (PAC), no selamento marginal de restaurações classe V em resina composta com margens localizadas em dentina. Setenta e cinco incisivos bovinos receberam preparos de cavidades classe V, na raiz, com o intuito de situar as margens cavitárias em dentina. Os dentes foram divididos em cinco grupos de acordo com o método de fotoativação. As cavidades, depois de condicionadas, foram tratadas com o sistema adesivo Single Bond (3M Dental) e restauradas com a resina composta Z100 (3M Dental) pela técnica incremental. A fotoativação foi realizada para cada grupo como descrito a seguir: Grupo I: PAC pelo método de fotoativação constante: 1600mW/cm² - 3s; Grupo II: PAC pelo método de fotoativação por passos (800mW/cm² - 2s, subindo automaticamente para 1600mW/cm² - 4s); Grupo III: QTH pelo método de fotoativação constante: 400 mW/cm² - 40s; Grupo IV: QTH pelo método de fotoativação em rampa: 100 a 600 mW/cm² - 15s, permanecendo a 600mW/cm2 por mais 25s; Grupo V: QTH pelo método de fotoativação por pulso: 200 mW/cm² - 3s, tempo de espera de 3min.e a seguir 600mW/cm² - 30s. Os dentes foram armazenados em água destilada a 37ºC por 30 dias e então submetidos à ciclagem térmica, por 500 ciclos à 5 ºC e 55 ºC. Os ápices dos dentes foram selados com resina composta e os dentes foram cobertos com duas camadas de esmalte para unha, antes da sua imersão em fucsina básica a 0,5%. Os dentes foram seccionados e os cortes foram escaneados para avaliação da área infiltrada por corante por um programa de computador (Image Tools). Os cortes foram também visualizados com lupa para a determinação do grau de penetração do corante na interface dente-restauração por escores. Diferenças estatisticamente significantes foram observadas entre os grupos quanto ao grau e à área de penetração de corante (p < 0,05). Os grupos I e II apresentaram valores significantemente mais altos de infiltração e penetração do corante que os grupos III, IV e V. Em conclusão, o uso da fonte de PAC, no modo constante e por passos, resultou em valores significantemente maiores de infiltração marginal quando comparados com a intensidade de luz média emitida pelos aparelhos de QTH. Os métodos de fotoativação por pulso, rampa e continuo com a fonte de QTH resultaram num grau similar de microinfiltração. |
| first_indexed | 2024-04-14T01:40:02Z |
| format | Article |
| id | doaj.art-051ed4a23f0a4dbab71d74966f992bf7 |
| institution | Directory Open Access Journal |
| issn | 1678-7757 1678-7765 |
| language | English |
| last_indexed | 2024-04-14T01:40:02Z |
| publishDate | 2005-06-01 |
| publisher | University of São Paulo |
| record_format | Article |
| series | Journal of Applied Oral Science |
| spelling | doaj.art-051ed4a23f0a4dbab71d74966f992bf72022-12-22T02:19:47ZengUniversity of São PauloJournal of Applied Oral Science1678-77571678-77652005-06-0113219319710.1590/S1678-77572005000200019Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina compostaMaria Jacinta M. Coelho SantosMário Honorato da Silva e Souza JúniorGildo Coelho Santos JúniorOmar El-MowafyAna Paula Chedid CavalcantiCarla Farah NemeThe aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized class V cavities in all dentin margins. Teeth were divided into 5 equal groups according to the curing cycle. The cavities were incrementally restored with a composite resin (Single Bond/Z-100, 3M). Light curing was applied as follows: Group I: PAC light continuous-cycle curing at 1600 mW/cm² for 3s; Group II: PAC light step-cycle curing (2s at 800 mW/cm² then 4s at 1600 mW/cm²); Group III: QTH light continuous-cycle curing at 400 mW/cm² for 40s; Group IV: QTH light ramp-cycle curing (from 100 to 600 mW/cm² in 15s followed by 25s at 600 mW/cm²); Group V: QTH light pulse-delay curing (200 mW/cm² for 3s followed by 3 min delay then 600 mW/cm² for 30s). Teeth were stored in distilled water at 37ºC for 30 days and then subjected to thermocycling for 500 cycles at 5 and 55ºC. Root apices were sealed and teeth coated with nail varnish before they were immersed in 0.5% fuchsine red dye solution. Teeth were then sectioned and slices were scanned with a computer scanner to determine the area of dye leakage using a computer program (Image Tools). Images of tooth slices were also visually examined under magnification and dye penetration along the tooth/restoration interface was scored. Significant differences in the degree of dye penetration and leakage were detected between groups (p<.05). Groups I and II had significantly higher values of dye penetration and leakage than groups III, IV and V. In conclusion, the use of PAC light curing in a continuous or step cycle modes resulted in increased microleakage of Class V resin composite restorations compared with medium intensity QTH light curing. Pulse, ramp and continuous-cycle curing modes with QTH light resulted in similar degrees of microleakage.<br>O objetivo deste estudo foi determinar o efeito da polimerização gradual, mediante a utilização de aparelhos de Quartzo-Tungustênio-Halógena (QTH) e Arco de Plasma de Xenônio (PAC), no selamento marginal de restaurações classe V em resina composta com margens localizadas em dentina. Setenta e cinco incisivos bovinos receberam preparos de cavidades classe V, na raiz, com o intuito de situar as margens cavitárias em dentina. Os dentes foram divididos em cinco grupos de acordo com o método de fotoativação. As cavidades, depois de condicionadas, foram tratadas com o sistema adesivo Single Bond (3M Dental) e restauradas com a resina composta Z100 (3M Dental) pela técnica incremental. A fotoativação foi realizada para cada grupo como descrito a seguir: Grupo I: PAC pelo método de fotoativação constante: 1600mW/cm² - 3s; Grupo II: PAC pelo método de fotoativação por passos (800mW/cm² - 2s, subindo automaticamente para 1600mW/cm² - 4s); Grupo III: QTH pelo método de fotoativação constante: 400 mW/cm² - 40s; Grupo IV: QTH pelo método de fotoativação em rampa: 100 a 600 mW/cm² - 15s, permanecendo a 600mW/cm2 por mais 25s; Grupo V: QTH pelo método de fotoativação por pulso: 200 mW/cm² - 3s, tempo de espera de 3min.e a seguir 600mW/cm² - 30s. Os dentes foram armazenados em água destilada a 37ºC por 30 dias e então submetidos à ciclagem térmica, por 500 ciclos à 5 ºC e 55 ºC. Os ápices dos dentes foram selados com resina composta e os dentes foram cobertos com duas camadas de esmalte para unha, antes da sua imersão em fucsina básica a 0,5%. Os dentes foram seccionados e os cortes foram escaneados para avaliação da área infiltrada por corante por um programa de computador (Image Tools). Os cortes foram também visualizados com lupa para a determinação do grau de penetração do corante na interface dente-restauração por escores. Diferenças estatisticamente significantes foram observadas entre os grupos quanto ao grau e à área de penetração de corante (p < 0,05). Os grupos I e II apresentaram valores significantemente mais altos de infiltração e penetração do corante que os grupos III, IV e V. Em conclusão, o uso da fonte de PAC, no modo constante e por passos, resultou em valores significantemente maiores de infiltração marginal quando comparados com a intensidade de luz média emitida pelos aparelhos de QTH. Os métodos de fotoativação por pulso, rampa e continuo com a fonte de QTH resultaram num grau similar de microinfiltração.http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572005000200019Resinas compostasMicroinfiltraçãoPolimerizaçãoUnidades fotopolimerizadorasComposite resinsMicroleakagePolymerizationLight units |
| spellingShingle | Maria Jacinta M. Coelho Santos Mário Honorato da Silva e Souza Júnior Gildo Coelho Santos Júnior Omar El-Mowafy Ana Paula Chedid Cavalcanti Carla Farah Neme Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta Journal of Applied Oral Science Resinas compostas Microinfiltração Polimerização Unidades fotopolimerizadoras Composite resins Microleakage Polymerization Light units |
| title | Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta |
| title_full | Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta |
| title_fullStr | Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta |
| title_full_unstemmed | Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta |
| title_short | Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta |
| title_sort | influence of light intensity and curing cycle on microleakage of class v composite resin restorations influencia da intensidade de luz e metodos de fotoativacao no selamento marginal de restauracoes classe v em resina composta |
| topic | Resinas compostas Microinfiltração Polimerização Unidades fotopolimerizadoras Composite resins Microleakage Polymerization Light units |
| url | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572005000200019 |
| work_keys_str_mv | AT mariajacintamcoelhosantos influenceoflightintensityandcuringcycleonmicroleakageofclassvcompositeresinrestorationsinfluenciadaintensidadedeluzemetodosdefotoativacaonoselamentomarginalderestauracoesclassevemresinacomposta AT mariohonoratodasilvaesouzajunior influenceoflightintensityandcuringcycleonmicroleakageofclassvcompositeresinrestorationsinfluenciadaintensidadedeluzemetodosdefotoativacaonoselamentomarginalderestauracoesclassevemresinacomposta AT gildocoelhosantosjunior influenceoflightintensityandcuringcycleonmicroleakageofclassvcompositeresinrestorationsinfluenciadaintensidadedeluzemetodosdefotoativacaonoselamentomarginalderestauracoesclassevemresinacomposta AT omarelmowafy influenceoflightintensityandcuringcycleonmicroleakageofclassvcompositeresinrestorationsinfluenciadaintensidadedeluzemetodosdefotoativacaonoselamentomarginalderestauracoesclassevemresinacomposta AT anapaulachedidcavalcanti influenceoflightintensityandcuringcycleonmicroleakageofclassvcompositeresinrestorationsinfluenciadaintensidadedeluzemetodosdefotoativacaonoselamentomarginalderestauracoesclassevemresinacomposta AT carlafarahneme influenceoflightintensityandcuringcycleonmicroleakageofclassvcompositeresinrestorationsinfluenciadaintensidadedeluzemetodosdefotoativacaonoselamentomarginalderestauracoesclassevemresinacomposta |