Experimental Study on the Properties of Autoclave Curing High-Strength Concrete According to CaO/SiO<sub>2</sub> Ratio

Experimental Study on the Properties of Autoclave Curing High-Strength Concrete According to CaO/SiO<sub>2</sub> Ratio

In this experimental study, tests were conducted to obtain the CaO/SiO<sub>2</sub> (C/S) molar ratio that minimizes the micropores of hardened concrete. To this end, the compressive strength, thermogravimetric analysis (TGA), and microporous structure of hardened concrete were investigat...

ver descrição completa

Detalhes bibliográficos
Principais autores:	Jeongmin Ra, Sangchul Shin, Jinman Kim
Formato:	Artigo
Idioma:	English
Publicado em:	MDPI AG 2023-05-01
coleção:	Applied Sciences
Assuntos:	high-strength concrete calcium silicate hydrate C/S molar ratio autocalve curing micro strcuture
Acesso em linha:	https://www.mdpi.com/2076-3417/13/10/6190

Registros relacionados

Microstructure, Thermal Stability, and Catalytic Activity of Compounds Formed in CaO-SiO<sub>2</sub>-Cr(NO<sub>3</sub>)<sub>3</sub>-H<sub>2</sub>O System
por: Domante Niuniavaite, et al.
Publicado em: (2020-07-01)

Effect of curing regimes on strength of magnesium silicate hydrate cement
por: Xiao Luo, et al.
Publicado em: (2023-09-01)

Effect of Sodium Phosphate and Cellulose Ethers on MgO/SiO<sub>2</sub> Cements for the 3D Printing of Forsterite Bioceramics
por: Lorenzo Cheli, et al.
Publicado em: (2024-05-01)

Mineralogical, textural and physical-mechanical study of hydraulic lime mortars cured under different moisture conditions
por: A. Arizzi, et al.
Publicado em: (2015-06-01)

The Stabilization of Copper and Cadmium in The Hydrated CaO-CuO-SiO2 and CaO-CdO-SiO2 Composites
por: A. K. Prodjosantoso, Y. Febriadi, A. R. P. Utami and M. P. Utomo
Publicado em: (2024-06-01)

Influence of sodium nitrate on the phases formed in the MgO-Al2O3-SiO2-H2O system
por: Ellina Bernard, et al.
Publicado em: (2021-01-01)

Influence of Ceria Addition on Crystallization Behavior and Properties of Mesoporous Bioactive Glasses in the SiO<sub>2</sub>–CaO–P<sub>2</sub>O<sub>5</sub>–CeO<sub>2</sub> System
por: Elena Maria Anghel, et al.
Publicado em: (2022-05-01)

Influence of CaO Content on the Fly Ash–Lime System Hydrothermal Synthesis Reaction Under Autoclave Curing
por: Chenhui Zhu, et al.
Publicado em: (2021-11-01)

Composite Ceramics in the Na<sub>2</sub>O–CaO–SiO<sub>2</sub>–P<sub>2</sub>O<sub>5</sub> System Obtained from Pastes including Hydroxyapatite and an Aqueous Solution of Sodium Silicate
por: Maksim Kaimonov, et al.
Publicado em: (2022-09-01)

Study of the Structure of FeO<i>x</i>-CaO-SiO<sub>2</sub>-MgO and FeO<i>x</i>-CaO-SiO<sub>2</sub>-MgO-Cu<sub>2</sub>O-PdO Slags Relevant to Urban Ores Processing through Cu Smelting
por: Mohammad Mehedi Hasan, et al.
Publicado em: (2020-01-01)

The Effect of SrO Addition on the Recrystallization of ZrSiO<sub>4</sub> in Raw Glass–Ceramic Glazes from the SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-CaO-MgO-K<sub>2</sub>O-ZrO<sub>2</sub> System
por: Janusz Partyka, et al.
Publicado em: (2023-09-01)

Rheological Properties and Curing Characteristics of Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> Foam Slurries Containing Organic Gelling Agent
por: WANG Xin, et al.
Publicado em: (2017-12-01)

Connecting <i>SiO</i><sub>4</sub> in Silicate and Silicate Chain Networks to Compute Kulli Temperature Indices
por: Ying-Fang Zhang, et al.
Publicado em: (2022-11-01)

Effect of Iron-Doped TiO<sub>2</sub> Nanotubes on the Hydration of Tricalcium Silicate
por: S. Mohd. Yonos Qattali, et al.
Publicado em: (2023-06-01)

Atomistic Simulation Studies of Na<sub>4</sub>SiO<sub>4</sub>
por: Mallikage Shalani Shanika, et al.
Publicado em: (2024-08-01)

In vitro bioactivity of biphasic calcium phosphate silicate glassceramic in CaO-SiO2-P2O5 system
por: Lachezar Radev, et al.
Publicado em: (2010-03-01)

Synthesis and Crystal Structures of Two Crystalline Silicic Acids: Hydrated H-Apophyllite, H<sub>16</sub>Si<sub>16</sub>O<sub>40</sub> • 8–10 H<sub>2</sub>O and H-Carletonite, H<sub>32</sub>Si<sub>64</sub>O<sub>144</sub>
por: Bernd Marler, et al.
Publicado em: (2024-03-01)

Thermoelectric Generator Based on CuSO<sub>4</sub> and Na<sub>2</sub>SiO<sub>3</sub>
por: Mihail Chira, et al.
Publicado em: (2020-12-01)

Dissolution of CaO in SiO<sub>2</sub>-CaO-Al<sub>2</sub>O<sub>3</sub> Slag in Si Production
por: Marit Buhaug Folstad, et al.
Publicado em: (2024-02-01)

Mathematical Model of Autoclave Curing of Epoxy Resin Based Composite Materials
por: A. Abdul dnan, et al.
Publicado em: (2007-07-01)

Hydration behaviors of calcium silicate-based biomaterials
por: Yuan-Ling Lee, et al.
Publicado em: (2017-06-01)

Combustion Synthesis of Nanocrystalline Ba<sub>1.3</sub>Ca<sub>0.7</sub>SiO<sub>4</sub> Semiconductors Using Urea as an Energy Efficient Fuel
por: Desta R. Golja, et al.
Publicado em: (2023-01-01)

The influence of the curing conditions of concrete on durability after freeze-thaw accelerated testing
por: G. Al-Assadi, et al.
Publicado em: (2015-12-01)

Measurement of CaO-SiO2-SaCl2 slag density by an improved Archimedean method
por: Wang Y., et al.
Publicado em: (2015-01-01)

Strain-hardening magnesium-silicate-hydrate composites (SHMSHC) utilizing reactive magnesia cement (MgO) and calcined clay (metakaolin)
por: Kumar, Dhanendra, et al.
Publicado em: (2024)

The study on the interface reaction characteristics of different binary slag, CaO – MgO, Al<sub>2</sub>O<sub>3</sub> – CaO, Al<sub>2</sub>O<sub>3</sub> – MgO, SiO<sub>2</sub> – CaO, SiO<sub>2</sub> - MgO
por: R. R. Yin, et al.
Publicado em: (2019-01-01)

Effect of Size-Dependent Thermal Instability on Synthesis of Zn<sub>2</sub> SiO<sub>4</sub>-SiO<sub><it>x</it></sub> Core–Shell Nanotube Arrays and Their Cathodoluminescence Properties
por: Dierre Benjamin, et al.
Publicado em: (2010-01-01)

Improved hydration resistance of MgO–2CaO·SiO2–3CaO·SiO2 composite refractory using low-grade minerals
por: Xuewu Zhan, et al.
Publicado em: (2020-01-01)

Effect of <i>n</i>(SiO<sub>2</sub>)/<i>n</i>(Al<sub>2</sub>O<sub>3</sub>) molar ratio on physical properties and microstructure of foamed geopolymer
por: Rui Yafeng, et al.
Publicado em: (2019-06-01)

The Early Age Hydration Products and Mechanical Properties of Cement Paste Containing GBFS under Steam Curing Condition
por: Baoliang Li, et al.
Publicado em: (2022-10-01)

Performance of Autoclaved Concrete with Iron Tailings
por: Zhenzhen Geng, et al.
Publicado em: (2023-12-01)

Phase relations of NASICON materials and compilation of the quaternary phase diagram Na<sub>2</sub>O-P<sub>2</sub>O<sub>5</sub>-SiO<sub>2</sub>-ZrO<sub>2</sub>
por: Frank Tietz
Publicado em: (2017-12-01)

Materials in the CaO-K<sub>2</sub>O-SO<sub>3</sub>-H<sub>2</sub>O System Based on Powder Mixtures including Calciolangbeinite K<sub>2</sub>Ca<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> and Calcium Sulfate Anhydrite CaSO<sub>4</sub>
por: Alexander I. Kuznetsov, et al.
Publicado em: (2023-07-01)

INFLUENCE OF CURING CONDITIONS ON THE EARLY STRENGTH OF LOW TEMPERATURE BELITE CEMENTS
por: Sambo Gwandu Haliru, et al.
Publicado em: (2024-01-01)

Bragg Grating Assisted Sagnac Interferometer in SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-La<sub>2</sub>O<sub>3</sub> Polarization-Maintaining Fiber for Strain–Temperature Discrimination
por: Zhifang Wu, et al.
Publicado em: (2020-08-01)

Enhancing hydration and internal curing in cementitious mixes: The impact of pre-treated milkweed fibres
por: Amirmohammad Sabziparvar, et al.
Publicado em: (2024-07-01)

Hydration behavior and formation of strätlingite compound (C2ASH8) in a bio-cement based on tri-calcium silicate and mono-calcium aluminate for dental applications: influence of curing medium
por: M. M. Radwan, et al.
Publicado em: (2022-06-01)

Mathematical Model for Autoclave Curing of Unsaturated Polyester Based Composite Materials
por: Adnan A. Abdul Razak
Publicado em: (2010-03-01)

Mathematical Model For Autoclave Curing Of Unsaturated Polyester Based Composite Materials
por: Adnan A. Abdul Razak
Publicado em: (2013-05-01)

Effect of CaO/ SiO<sub>2</sub> ratio on viscosity and structure of slag
por: L. Řeháčková, et al.
Publicado em: (2015-07-01)