Experimental Study on the Properties of Autoclave Curing High-Strength Concrete According to CaO/SiO<sub>2</sub> Ratio

Experimental Study on the Properties of Autoclave Curing High-Strength Concrete According to CaO/SiO<sub>2</sub> Ratio

In this experimental study, tests were conducted to obtain the CaO/SiO<sub>2</sub> (C/S) molar ratio that minimizes the micropores of hardened concrete. To this end, the compressive strength, thermogravimetric analysis (TGA), and microporous structure of hardened concrete were investigat...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Jeongmin Ra, Sangchul Shin, Jinman Kim
Định dạng:	Bài viết
Ngôn ngữ:	English
Được phát hành:	MDPI AG 2023-05-01
Loạt:	Applied Sciences
Những chủ đề:	high-strength concrete calcium silicate hydrate C/S molar ratio autocalve curing micro strcuture
Truy cập trực tuyến:	https://www.mdpi.com/2076-3417/13/10/6190

Những quyển sách tương tự

Microstructure, Thermal Stability, and Catalytic Activity of Compounds Formed in CaO-SiO<sub>2</sub>-Cr(NO<sub>3</sub>)<sub>3</sub>-H<sub>2</sub>O System
Bằng: Domante Niuniavaite, et al.
Được phát hành: (2020-07-01)

Effect of curing regimes on strength of magnesium silicate hydrate cement
Bằng: Xiao Luo, et al.
Được phát hành: (2023-09-01)

Effect of Sodium Phosphate and Cellulose Ethers on MgO/SiO<sub>2</sub> Cements for the 3D Printing of Forsterite Bioceramics
Bằng: Lorenzo Cheli, et al.
Được phát hành: (2024-05-01)

Mineralogical, textural and physical-mechanical study of hydraulic lime mortars cured under different moisture conditions
Bằng: A. Arizzi, et al.
Được phát hành: (2015-06-01)

The Stabilization of Copper and Cadmium in The Hydrated CaO-CuO-SiO2 and CaO-CdO-SiO2 Composites
Bằng: A. K. Prodjosantoso, Y. Febriadi, A. R. P. Utami and M. P. Utomo
Được phát hành: (2024-06-01)

Influence of sodium nitrate on the phases formed in the MgO-Al2O3-SiO2-H2O system
Bằng: Ellina Bernard, et al.
Được phát hành: (2021-01-01)

Influence of Ceria Addition on Crystallization Behavior and Properties of Mesoporous Bioactive Glasses in the SiO<sub>2</sub>–CaO–P<sub>2</sub>O<sub>5</sub>–CeO<sub>2</sub> System
Bằng: Elena Maria Anghel, et al.
Được phát hành: (2022-05-01)

Influence of CaO Content on the Fly Ash–Lime System Hydrothermal Synthesis Reaction Under Autoclave Curing
Bằng: Chenhui Zhu, et al.
Được phát hành: (2021-11-01)

Composite Ceramics in the Na<sub>2</sub>O–CaO–SiO<sub>2</sub>–P<sub>2</sub>O<sub>5</sub> System Obtained from Pastes including Hydroxyapatite and an Aqueous Solution of Sodium Silicate
Bằng: Maksim Kaimonov, et al.
Được phát hành: (2022-09-01)

Study of the Structure of FeO<i>x</i>-CaO-SiO<sub>2</sub>-MgO and FeO<i>x</i>-CaO-SiO<sub>2</sub>-MgO-Cu<sub>2</sub>O-PdO Slags Relevant to Urban Ores Processing through Cu Smelting
Bằng: Mohammad Mehedi Hasan, et al.
Được phát hành: (2020-01-01)

The Effect of SrO Addition on the Recrystallization of ZrSiO<sub>4</sub> in Raw Glass–Ceramic Glazes from the SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-CaO-MgO-K<sub>2</sub>O-ZrO<sub>2</sub> System
Bằng: Janusz Partyka, et al.
Được phát hành: (2023-09-01)

Rheological Properties and Curing Characteristics of Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> Foam Slurries Containing Organic Gelling Agent
Bằng: WANG Xin, et al.
Được phát hành: (2017-12-01)

Connecting <i>SiO</i><sub>4</sub> in Silicate and Silicate Chain Networks to Compute Kulli Temperature Indices
Bằng: Ying-Fang Zhang, et al.
Được phát hành: (2022-11-01)

Effect of Iron-Doped TiO<sub>2</sub> Nanotubes on the Hydration of Tricalcium Silicate
Bằng: S. Mohd. Yonos Qattali, et al.
Được phát hành: (2023-06-01)

Atomistic Simulation Studies of Na<sub>4</sub>SiO<sub>4</sub>
Bằng: Mallikage Shalani Shanika, et al.
Được phát hành: (2024-08-01)

In vitro bioactivity of biphasic calcium phosphate silicate glassceramic in CaO-SiO2-P2O5 system
Bằng: Lachezar Radev, et al.
Được phát hành: (2010-03-01)

Synthesis and Crystal Structures of Two Crystalline Silicic Acids: Hydrated H-Apophyllite, H<sub>16</sub>Si<sub>16</sub>O<sub>40</sub> • 8–10 H<sub>2</sub>O and H-Carletonite, H<sub>32</sub>Si<sub>64</sub>O<sub>144</sub>
Bằng: Bernd Marler, et al.
Được phát hành: (2024-03-01)

Thermoelectric Generator Based on CuSO<sub>4</sub> and Na<sub>2</sub>SiO<sub>3</sub>
Bằng: Mihail Chira, et al.
Được phát hành: (2020-12-01)

Dissolution of CaO in SiO<sub>2</sub>-CaO-Al<sub>2</sub>O<sub>3</sub> Slag in Si Production
Bằng: Marit Buhaug Folstad, et al.
Được phát hành: (2024-02-01)

Mathematical Model of Autoclave Curing of Epoxy Resin Based Composite Materials
Bằng: A. Abdul dnan, et al.
Được phát hành: (2007-07-01)

Hydration behaviors of calcium silicate-based biomaterials
Bằng: Yuan-Ling Lee, et al.
Được phát hành: (2017-06-01)

Combustion Synthesis of Nanocrystalline Ba<sub>1.3</sub>Ca<sub>0.7</sub>SiO<sub>4</sub> Semiconductors Using Urea as an Energy Efficient Fuel
Bằng: Desta R. Golja, et al.
Được phát hành: (2023-01-01)

The influence of the curing conditions of concrete on durability after freeze-thaw accelerated testing
Bằng: G. Al-Assadi, et al.
Được phát hành: (2015-12-01)

Measurement of CaO-SiO2-SaCl2 slag density by an improved Archimedean method
Bằng: Wang Y., et al.
Được phát hành: (2015-01-01)

Strain-hardening magnesium-silicate-hydrate composites (SHMSHC) utilizing reactive magnesia cement (MgO) and calcined clay (metakaolin)
Bằng: Kumar, Dhanendra, et al.
Được phát hành: (2024)

The study on the interface reaction characteristics of different binary slag, CaO – MgO, Al<sub>2</sub>O<sub>3</sub> – CaO, Al<sub>2</sub>O<sub>3</sub> – MgO, SiO<sub>2</sub> – CaO, SiO<sub>2</sub> - MgO
Bằng: R. R. Yin, et al.
Được phát hành: (2019-01-01)

Effect of Size-Dependent Thermal Instability on Synthesis of Zn<sub>2</sub> SiO<sub>4</sub>-SiO<sub><it>x</it></sub> Core–Shell Nanotube Arrays and Their Cathodoluminescence Properties
Bằng: Dierre Benjamin, et al.
Được phát hành: (2010-01-01)

Improved hydration resistance of MgO–2CaO·SiO2–3CaO·SiO2 composite refractory using low-grade minerals
Bằng: Xuewu Zhan, et al.
Được phát hành: (2020-01-01)

Effect of <i>n</i>(SiO<sub>2</sub>)/<i>n</i>(Al<sub>2</sub>O<sub>3</sub>) molar ratio on physical properties and microstructure of foamed geopolymer
Bằng: Rui Yafeng, et al.
Được phát hành: (2019-06-01)

The Early Age Hydration Products and Mechanical Properties of Cement Paste Containing GBFS under Steam Curing Condition
Bằng: Baoliang Li, et al.
Được phát hành: (2022-10-01)

Performance of Autoclaved Concrete with Iron Tailings
Bằng: Zhenzhen Geng, et al.
Được phát hành: (2023-12-01)

Phase relations of NASICON materials and compilation of the quaternary phase diagram Na<sub>2</sub>O-P<sub>2</sub>O<sub>5</sub>-SiO<sub>2</sub>-ZrO<sub>2</sub>
Bằng: Frank Tietz
Được phát hành: (2017-12-01)

Materials in the CaO-K<sub>2</sub>O-SO<sub>3</sub>-H<sub>2</sub>O System Based on Powder Mixtures including Calciolangbeinite K<sub>2</sub>Ca<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> and Calcium Sulfate Anhydrite CaSO<sub>4</sub>
Bằng: Alexander I. Kuznetsov, et al.
Được phát hành: (2023-07-01)

INFLUENCE OF CURING CONDITIONS ON THE EARLY STRENGTH OF LOW TEMPERATURE BELITE CEMENTS
Bằng: Sambo Gwandu Haliru, et al.
Được phát hành: (2024-01-01)

Bragg Grating Assisted Sagnac Interferometer in SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-La<sub>2</sub>O<sub>3</sub> Polarization-Maintaining Fiber for Strain–Temperature Discrimination
Bằng: Zhifang Wu, et al.
Được phát hành: (2020-08-01)

Enhancing hydration and internal curing in cementitious mixes: The impact of pre-treated milkweed fibres
Bằng: Amirmohammad Sabziparvar, et al.
Được phát hành: (2024-07-01)

Hydration behavior and formation of strätlingite compound (C2ASH8) in a bio-cement based on tri-calcium silicate and mono-calcium aluminate for dental applications: influence of curing medium
Bằng: M. M. Radwan, et al.
Được phát hành: (2022-06-01)

Mathematical Model for Autoclave Curing of Unsaturated Polyester Based Composite Materials
Bằng: Adnan A. Abdul Razak
Được phát hành: (2010-03-01)

Mathematical Model For Autoclave Curing Of Unsaturated Polyester Based Composite Materials
Bằng: Adnan A. Abdul Razak
Được phát hành: (2013-05-01)

Effect of CaO/ SiO<sub>2</sub> ratio on viscosity and structure of slag
Bằng: L. Řeháčková, et al.
Được phát hành: (2015-07-01)