Microstructure transition of γ-TiAl alloys with abrupt cross-sections in yttria ceramic moulds during directional solidification by electromagnetic cold crucible
Directional solidification of γ-TiAl alloys with abruptly varying cross-sections was performed in yttria molds using an electromagnetic cold crucible. The solid–liquid interface at different growth positions was revealed by quenching using a liquid metal coolant, and the temperature field was mapped...
Main Authors: | Haitao Huang, Hongsheng Ding, Xuesong Xu, Ruirun Chen, Jingjie Guo, Hengzhi Fu |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2022-07-01
|
Series: | Journal of Materials Research and Technology |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785422007177 |
Similar Items
-
Continuous melting and directional solidification of silicon ingot with an electromagnetic cold crucible
by: Huang Feng, et al.
Published: (2012-02-01) -
Temperature-dependent mechanical properties and fracture behavior of directionally solidified Ti47Al2Cr2Nb alloy
by: Yongzhe Wang, et al.
Published: (2023-07-01) -
Review on Progress of Lamellar Orientation Control in Directionally Solidified TiAl Alloys
by: Han Liu, et al.
Published: (2023-07-01) -
Microstructure and Properties of TiAl-Based Alloys Melted in Graphite Crucible
by: Wojciech Szkliniarz, et al.
Published: (2021-04-01) -
Microstructure Evolution of Gas-Atomized β-Solidifying γ-TiAl Alloy Powder during Subsequent Heat Treatment
by: Sung-Hyun Park, et al.
Published: (2023-11-01)