Investigations of 2D PtS<sub>2</sub>’s Saturable Absorption Characteristic and Its Optimization to OPO’s Operation
A 6.2 nm-thickness platinum disulfide (PtS<sub>2</sub>) film was prepared by electron beam evaporation with post vulcanization. The nonlinear transmittance was measured by power scanning method and the modulation depth is fitted to be 13%. Based on the transmittance curve, saturable abso...
Main Authors: | Xinyu Hu, Jing Wang, Heze Guo, Kai Jiang, Wenjing Tang, Wei Xia |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-05-01
|
Series: | Nanomaterials |
Subjects: | |
Online Access: | https://www.mdpi.com/2079-4991/12/10/1670 |
Similar Items
-
Stacking-Mediated Type-I/Type-II Transition in Two-Dimensional MoTe<sub>2</sub>/PtS<sub>2</sub> Heterostructure: A First-Principles Simulation
by: Kai Ren, et al.
Published: (2022-03-01) -
Fabrication of Large-Area Short-Wave Infrared Array Photodetectors under High Operating Temperature by High Quality PtS<sub>2</sub> Continuous Films
by: Yichen Zhang, et al.
Published: (2022-03-01) -
Experimental evaluation of lime spray drying for SO<sub>2</sub> absorption
by: Lawrence Koech, et al.
Published: (2023-04-01) -
Ultralight MOF-Derived Ni<sub>3</sub>S<sub>2</sub>@N, S-Codoped Graphene Aerogels for High-Performance Microwave Absorption
by: Wenjing Yu, et al.
Published: (2022-02-01) -
NO<sub>2</sub> Sensing Capability of Pt–Au–SnO<sub>2</sub> Composite Nanoceramics at Room Temperature
by: Jiannan Song, et al.
Published: (2023-02-01)