Modeling the Constitutive Relationship of Al–0.62Mg–0.73Si Alloy Based on Artificial Neural Network

Modeling the Constitutive Relationship of Al–0.62Mg–0.73Si Alloy Based on Artificial Neural Network

In this work, the hot deformation behavior of 6A02 aluminum alloy was investigated by isothermal compression tests conducted in the temperature range of 683–783 K and strain-rate range of 0.001–1 s−1. According to the obtained true stress–true strain curves, the constitutive relationship of the allo...

Full description

Bibliographic Details
Main Authors:	Ying Han, Shun Yan, Yu Sun, Hua Chen
Format:	Article
Language:	English
Published:	MDPI AG 2017-03-01
Series:	Metals
Subjects:	deformation behavior constitutive model BP neural network aluminum alloy
Online Access:	http://www.mdpi.com/2075-4701/7/4/114

Similar Items

Hot deformation behavior and constitutive equation of Mg-9Al-3Si-0.375Sr-0.78Y alloy
by: ZHANG Lian-teng, et al.
Published: (2021-02-01)

Microstructure evolution and constitutive modeling of as-cast A356 aluminum alloy in semi-solid deformation regime
by: A.H. Boluri Gashti, et al.
Published: (2023-05-01)

Wire for solid, cold-forged rivets of aluminium-copper-magnesium-silicon-manganese alloy (Not exceeding 10 mm diameter) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
by: 8096 British Standards Institution

Microstructural and constitutive relationship in process modeling of hot working: The case of a 60Mg-30Pb-9.2Al-0.8B magnesium alloy
by: Bo Li, et al.
Published: (2023-09-01)

Damage by the cracking of silicon particles in an Al-7Si-0.4Mg casting alloy /
by: 416838 Caceres, C. H., et al.

Constitutive equation and microstructure evaluation of an extruded aluminum alloy
by: Saravanan L, et al.
Published: (2016-01-01)

Sheet and strip of aluminium-magnesium-silicon-manganese alloy (Solution treated and precipitation treated)(Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
by: 8096 British Standards Institution

Warm Tensile Deformation Behavior and Constitutive Equation of Supersaturated Solid-Solutionized Al-9Mg Extruded Alloy
by: Seung Y. Yang, et al.
Published: (2021-12-01)

Effect of Al-5Ti-0.62C-0.2Ce Master Alloy on the Microstructure and Tensile Properties of Commercial Pure Al and Hypoeutectic Al-8Si Alloy
by: Wanwu Ding, et al.
Published: (2017-06-01)

Sheet and strip of aluminium-magnesium-silicon-manganese alloy (Solution treated and precipitation treated) (Suitable for welding) (Mg 0.8, Si 1, Mn 0.7)
by: 8096 British Standards Institution

Room temperature strengthening mechanisms, high temperature deformation behavior and constitutive modeling in an Al-3.25Mg-0.37Zr-0.28Mn-0.19Y alloy
by: Furong Cao, et al.
Published: (2022-05-01)

Wire for solid, cold-forged rivets of aluminium-copper-magnesium-silicon-manganese alloy : for use in the solution treated and naturally aged condition (not exceeding 10mm diameter) (Cu4.4, Mg 0.5, Si 0.7, Mn 0.8) (2014A)
by: 8096 British Standards Institution

Sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and artificially aged) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and artificially aged) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Forging stock and forgings of aluminium-magnesium-silicon-manganese alloy (Solution treated and precipitation treated) (Suitable for welding) (Mg 0.8, Si 1, Mn 0.7)
by: 8096 British Standards Institution

Hot Deformation Behavior of Novel Al-Cu-Y(Er)-Mg-Mn-Zr Alloys
by: Maxim G. Khomutov, et al.
Published: (2021-09-01)

The hot deformation behavior and microstructural evolution of as-cast Mg–2Zn–0.5Mn–0.2Ca–0.3Nd–0.7La alloy
by: Jie Mi, et al.
Published: (2023-01-01)

Sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
by: 8096 British Standards Institution

Plate of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated, controlled stretched and percipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
by: 8096 British Standards Institution

Ingots and castings of aluminium-silicon-magnesium alloy (Solution treated and precipitation treated) (Si 7, Mg 0.3)
by: 8096 British Standards Institution

Forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
by: 8096 British Standards Institution

Aluminium-coated sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and artificially aged) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Aluminium-coated sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Supplied for solution treatment by the user) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Close toleranced sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy. (Solution treated and artificially aged) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Sheet and strip of aluminium-coated aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and artificially aged) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Hot compression deformation behavior and processing maps of Al–0.5Mg–0.4Si–0.1Cu alloy
by: Hui Yi, et al.
Published: (2022-07-01)

Effect of modification on the aluminium matrix of Al-Si-Mg alloys /
by: 270689 Ooi, Thean Joo
Published: (1999)

Microstructural evolution characteristics and a unified dislocation-density related constitutive model for a 7046 aluminum alloy during hot tensile
by: Daoguang He, et al.
Published: (2023-07-01)

Microstructural Analysis and Constitutive Modeling of Superplastic Deformation Behavior of Al-Mg-Zn-Cu-Zr-xNi Alloys with Different Ni Contents
by: Zarnigor S. Turaeva, et al.
Published: (2025-01-01)

Aluminium-coated sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Close toleranced sheet and strip of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Sheet and strip of aluminium-coated aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and aged at room tempreture) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Close toleranced sheet and strip of aluminium-coated aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and artificially aged) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Plate of aluminium-magnesium-silicon-manganese alloy (Solution treated, controlled stretched and precipitation treated) (Not exceeding 25 mm thickness) (Suitable for welding) (Mg 0.8, Si 1, Mn 0.7)
by: 8096 British Standards Institution

Close toleranced sheet and strip of aluminium-coated aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Effects of Al-5Ti-0.62C-1.07La intermediate alloy on the microstructure and mechanical properties of A356 aluminum alloy
by: Wanwu Ding, et al.
Published: (2020-01-01)

Sheet and strip of aluminium-coated aluminium-copper-magnesium-silicon-manganese alloy (Solution treated, cold worked for flattening and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.8, Mn 0.8)
by: 8096 British Standards Institution

Tube of aluminium-copper-magnesium-silicon-manganese alloy (Solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
by: 8096 British Standards Institution

Sheet and strip of aluminium-manganese alloy. (Soft - 0)
by: 8096 British Standards Institution