| Summary: | In this work, aramid nanofibers (ANFs)/reduced graphene oxide (ANFs/RGO) film electrodes were prepared by vacuum-assisted filtration, followed by hydroiodic acid reduction. Compared with thermal reduced ANFs/RGO, these as-prepared film electrodes exhibit a combination of mechanical and electrochemical properties with a tensile strength of 184.5 MPa and a volumetric specific capacitance of 134.4 F/cm<sup>3</sup> at a current density of 0.125 mA/cm<sup>2</sup>, respectively. In addition, the film electrodes also show a superior cycle life with 94.6% capacitance retention after 5000 cycles. This kind of free-standing film electrode may have huge potential for flexible energy-storage devices.
|
|---|