| Summary: | A carbon-supersaturated (CS-) high-speed steel punch was prepared using low-temperature plasma carburizing for fine blanking of pure titanium plates. The bare high-speed steel punch was also prepared as a reference to describe the adhesion and abrasive galling in the fine blanking of the titanium plates, even in a single shot. The CS-punch was free from severe chemical galling, even after repeatedly fine-blanking the pure titanium plates. A microstructure analysis, element mapping and a chemical composition analysis demonstrated that titanium debris fragments slightly deposited at the CS-punch edges in the presence of agglomerated free-carbon film due to the CS-punch. This galling-free fine-blanking behavior came from the in situ formation of free carbon tribofilms. This in situ lubrication resulted in the completely burnished surfaces of pure titanium blanks.
|
|---|