CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES
The aim of this study was to investigate the corrosion behaviour of annealed stainless steel mesh. Thermal oxidation treatments were applied to steel mesh in a muffle furnace at 500 ᵒC, 700 ᵒC and 900 ᵒC. Surface morphology of annealed and non-annealed stainless steel meshes was compared before and...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Bursa Uludag University
2020-04-01
|
| Series: | Uludağ University Journal of The Faculty of Engineering |
| Subjects: | |
| Online Access: | https://dergipark.org.tr/tr/pub/uumfd/issue/52836/597448 |
| _version_ | 1797912549544427520 |
|---|---|
| author | Sitki Aktas Kaan Kaplan Abdulcabbar Yavuz |
| author_facet | Sitki Aktas Kaan Kaplan Abdulcabbar Yavuz |
| author_sort | Sitki Aktas |
| collection | DOAJ |
| description | The aim of this study was to investigate the
corrosion behaviour of annealed stainless steel mesh. Thermal oxidation
treatments were applied to steel mesh in a muffle furnace at 500 ᵒC, 700 ᵒC and
900 ᵒC. Surface morphology of annealed and non-annealed stainless steel meshes
was compared before and after polarization. Roughness of the steel surface was
increased after heat-treatment. The corrosion properties of non-annealed and
annealed steel were determined using linear sweep voltammetry. The corrosion behaviour
of annealed stainless steel was examined by means of a potentiostat in a 3.5
wt.% NaCl, 1 M H2SO4 and 1 M KOH electrolytes. The corrosion susceptibility of heat treated
stainless steel was more than that of non-heat treated stainless steel in
alkaline electrolyte. While pitting corrosion of non-annealed and annealed
stainless steel was different, corrosion potential and current of steel mesh
without heat treatment was the same as the steel meshes annealed at 500 ᵒC and
700 ᵒC. Corrosion current and corrosion potential of non-annealed steel was the
same as 500 ᵒC annealed steel mesh in acidic medium. |
| first_indexed | 2024-04-10T11:57:41Z |
| format | Article |
| id | doaj.art-09dd1d315f274071a118e584bc491432 |
| institution | Directory Open Access Journal |
| issn | 2148-4147 2148-4155 |
| language | English |
| last_indexed | 2024-04-10T11:57:41Z |
| publishDate | 2020-04-01 |
| publisher | Bursa Uludag University |
| record_format | Article |
| series | Uludağ University Journal of The Faculty of Engineering |
| spelling | doaj.art-09dd1d315f274071a118e584bc4914322023-02-15T16:16:45ZengBursa Uludag UniversityUludağ University Journal of The Faculty of Engineering2148-41472148-41552020-04-0125150151010.17482/uumfd.5974481779CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTESSitki Aktas0Kaan Kaplan1Abdulcabbar Yavuz2GİRESUN ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, MAKİNE MÜHENDİSLİĞİ BÖLÜMÜGAZİANTEP ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, FİZİK MÜHENDİSLİĞİ BÖLÜMÜGAZİANTEP ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, METALURJİ VE MALZEME MÜHENDİSLİĞİ BÖLÜMÜThe aim of this study was to investigate the corrosion behaviour of annealed stainless steel mesh. Thermal oxidation treatments were applied to steel mesh in a muffle furnace at 500 ᵒC, 700 ᵒC and 900 ᵒC. Surface morphology of annealed and non-annealed stainless steel meshes was compared before and after polarization. Roughness of the steel surface was increased after heat-treatment. The corrosion properties of non-annealed and annealed steel were determined using linear sweep voltammetry. The corrosion behaviour of annealed stainless steel was examined by means of a potentiostat in a 3.5 wt.% NaCl, 1 M H2SO4 and 1 M KOH electrolytes. The corrosion susceptibility of heat treated stainless steel was more than that of non-heat treated stainless steel in alkaline electrolyte. While pitting corrosion of non-annealed and annealed stainless steel was different, corrosion potential and current of steel mesh without heat treatment was the same as the steel meshes annealed at 500 ᵒC and 700 ᵒC. Corrosion current and corrosion potential of non-annealed steel was the same as 500 ᵒC annealed steel mesh in acidic medium.https://dergipark.org.tr/tr/pub/uumfd/issue/52836/597448korozyonpaslanmaz çelikisıl i̇şlemisıl oksidasyoncorrosionstainless steelheat-treatmentthermal oxidation |
| spellingShingle | Sitki Aktas Kaan Kaplan Abdulcabbar Yavuz CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES Uludağ University Journal of The Faculty of Engineering korozyon paslanmaz çelik isıl i̇şlem isıl oksidasyon corrosion stainless steel heat-treatment thermal oxidation |
| title | CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES |
| title_full | CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES |
| title_fullStr | CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES |
| title_full_unstemmed | CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES |
| title_short | CORROSION BEHAVIOR OF ANNEALED STAINLESS STEEL MESH IN DIFFERENT ELECTROLYTES |
| title_sort | corrosion behavior of annealed stainless steel mesh in different electrolytes |
| topic | korozyon paslanmaz çelik isıl i̇şlem isıl oksidasyon corrosion stainless steel heat-treatment thermal oxidation |
| url | https://dergipark.org.tr/tr/pub/uumfd/issue/52836/597448 |
| work_keys_str_mv | AT sitkiaktas corrosionbehaviorofannealedstainlesssteelmeshindifferentelectrolytes AT kaankaplan corrosionbehaviorofannealedstainlesssteelmeshindifferentelectrolytes AT abdulcabbaryavuz corrosionbehaviorofannealedstainlesssteelmeshindifferentelectrolytes |