Optical and Electrical Properties of (002)-Oriented ZnO Films Prepared on Amorphous Substrates by Sol-Gel Spin-Coating
Zinc oxide (ZnO) films were prepared on amorphous quartz substrates by sol-gel spin-coating using Zn(CH3COO)2•2H2O precursor. Isopropanol, ethanol and 2-methoxyethanol were used as solvents. The film drying temperature was kept constant at 200 ºC and the annealing temperature was varied from 400 to...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2016-12-01
|
| Series: | Materials Research |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392016000700113&tlng=en |
| Summary: | Zinc oxide (ZnO) films were prepared on amorphous quartz substrates by sol-gel spin-coating using Zn(CH3COO)2•2H2O precursor. Isopropanol, ethanol and 2-methoxyethanol were used as solvents. The film drying temperature was kept constant at 200 ºC and the annealing temperature was varied from 400 to 800 ºC. Highly transparent and (002)-oriented hexagonal wurtzite-type ZnO films were obtained using isopropanol solvent. The ZnO films prepared at Tanneal = 600 ºC showed the highest (002) preferential orientation, however it was not the significant feature to achieve low resistivity. The uniform and (002)-oriented ZnO films prepared at Tanneal = 400 ºC display the highest transmittance (>93% in the visible region) and the lowest resistivity (7.1 Ω•cm). |
|---|---|