Determination of Crystal Growth Geometry Factors and Nucleation Site Densities of Electrodeposited Ferromagnetic Cobalt Nanowire Arrays
The time-dependence of electrochemical reduction current, which was observed during the one-dimensional (1-D) crystal growth of ferromagnetic cobalt nanowire arrays, was analyzed by Johnson–Mehl–Avrami–Kolmogorov (JMAK) theory. Textured hcp-Co nanowire arrays were synth...
Main Authors: | Ryusei Saeki, Takeshi Ohgai |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-03-01
|
Series: | Crystals |
Subjects: | |
Online Access: | http://www.mdpi.com/2073-4352/9/3/142 |
Similar Items
-
Heterogeneous Substrates Modify Non-Classical Nucleation Pathways: Reanalysis of Kinetic Data from the Electrodeposition of Mercury on Platinum Using Hierarchy of Sigmoid Growth Models
by: Viktoria Kleshtanova, et al.
Published: (2023-12-01) -
Effect of Uniaxial Compressive Stress on Phase Transformation Kinetics of Low-Carbon Steel
by: Shanchao Zuo, et al.
Published: (2022-06-01) -
Microhardness and heat-resistance performance of ferromagnetic cobalt-molybdenum nanocrystals electrodeposited from an aqueous solution containing citric acid
by: Tomoyuki Matsuda, et al.
Published: (2022-01-01) -
The Diminishing Role of the Nucleation Rate as Crystallization Develops in Avrami-Type Models
by: Fernando C. Pérez-Cárdenas
Published: (2022-08-01) -
Study on Precipitation Processes and Phase Transformation Kinetics of Iron Phosphate Dihydrate
by: Huiqi Wang, et al.
Published: (2022-09-01)