Phase Formation and High-Temperature Stability of Very Thin Co-Sputtered Ti-Al and Multilayered Ti/Al Films on Thermally Oxidized Si Substrates
Ti-Al thin films with a thickness of 200 nm were prepared either by co-sputtering from elemental Ti and Al targets or as Ti/Al multilayers with 10 and 20 nm individual layer thickness on thermally oxidized Si substrates. Some of the films were covered with a 20-nm-thick SiO<inline-formula> <...
Main Authors: | Marietta Seifert, Eric Lattner, Siegfried B. Menzel, Steffen Oswald, Thomas Gemming |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-04-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/13/9/2039 |
Similar Items
-
Durability of TiAl based surface acoustic wave devices for sensing at intermediate high temperatures
by: Marietta Seifert, et al.
Published: (2023-03-01) -
Mechanical properties and reciprocating sliding tribological behaviors of γ-TiAl substrate and plasma-based Mo–Si–Ti coating
by: Fengkun Li, et al.
Published: (2023-09-01) -
In-situ synthesized a dual-scale Ti2AlC reinforced TiAl composites with superior mechanical properties
by: Yupeng Wang, et al.
Published: (2024-01-01) -
Impact Resistance of Commercially Applied TiAl Alloys and Simple-Composition TiAl Alloys at Various Temperatures
by: Toshimitsu Tetsui
Published: (2022-11-01) -
Application of porous TiAl intermetallic compound in purification of industrial TiCl4 liquid in Ti metallurgy
by: Yao Jiang, et al.
Published: (2020-01-01)