Synthesis of alumina/YAG 20 vol% composite by co-precipitation
Co-precipitation of alumina/YAG precursor from aluminum and yttrium nitrate solution with ammonium carbonate results in dawsonite. Its crystallographic parameters differ from the compound precipitated with no yttrium additive. It suggests that yttrium ions become incorporated into the dawsonite stru...
Main Authors: | Radosław Lach, Krzysztof Haberko, Mirosław Bućko |
---|---|
Format: | Article |
Language: | English |
Published: |
University of Novi Sad
2011-12-01
|
Series: | Processing and Application of Ceramics |
Subjects: | |
Online Access: | http://www.tf.uns.ac.rs/publikacije/PAC/pdf/PAC%2014%2002.pdf |
Similar Items
-
Fabrication and mechanical characterization of YAG ceramic-composite with alumina nanoparticles using slip casting and sintering process
by: M Torki, et al.
Published: (2020-01-01) -
Effect of solid content on structure and properties of alumina ceramic matrix composite prepared by slurry infiltration method
by: DONG Ruilan, et al.
Published: (2023-08-01) -
Effect of LZSA glass-ceramic addition on the erosive wear of pressureless sintered alumina
by: Oscar Rubem K. Montedo, et al.
Published: (2020-04-01) -
Recycled Bottle Glass Wastes as Precursors for Porous Alumina Glass Ceramics Synthesis
by: Cosmin Vancea, et al.
Published: (2022-12-01) -
Electron Beam-Assisted Synthesis of YAG:Ce Ceramics
by: Zhakyp T. Karipbayev, et al.
Published: (2023-05-01)