Corrosion Resistance of Hsla Steel after Various Surface Treatments in Chloride Environment
The effect of mechanical and chemical surface treatment of high-strength low alloy steel S355J2 on its electrochemical characteristics was investigated by voltamperic tests in corrosive environment of 0.1M NaCl solution simulating sea atmosphere. Mechanical surface treatment was done by grinding on...
Main Authors: | Kamil Borko, Filip Pastorek, Stanislava Fintova, Branislav Hadzima |
---|---|
Format: | Article |
Language: | English |
Published: |
University of Žilina
2016-11-01
|
Series: | Communications |
Subjects: | |
Online Access: | https://komunikacie.uniza.sk/artkey/csl-201604-0015_corrosion-resistance-of-hsla-steel-after-various-surface-treatments-in-chloride-environment.php |
Similar Items
-
Effect of Phosphating Temperature on Surface Properties of Manganese Phosphate Coating on HSLA Steel
by: Jana Pastorkova, et al.
Published: (2020-01-01) -
Effect of the repair welding process on the microstructure and hardness of the T-JOINT S355J2+N steel
by: M. F. A. Sabana, et al.
Published: (2023-01-01) -
Cobalt-Doped Iron Phosphate Crystal on Stainless Steel Mesh for Corrosion-Resistant Oxygen Evolution Catalyst
by: Jaun An, et al.
Published: (2022-11-01) -
Microstructure and corrosion-wear resistance of laser cladding Al-Ni-TiC-CeO<sub>2</sub> composite coatings
by: HE Xing, et al.
Published: (2019-10-01) -
Corrosion behaviour of coated and non-coated steel with various microstructures /
by: Loh, Choong Young, 1985-, et al.
Published: (2009)