Building durable aqueous K-ion capacitors based on MXene family
Obtaining stable aqueous K-ion capacitors is still challenging due to the cathode materials tended to structurally collapse after long-term cycling during large-radius K-ion insertion/extraction. In this work, three different typical MXene electrodes, i.e., Nb2C, Ti2C, and Ti3C2 were individually in...
Main Authors: | Guojin Liang, Xinliang Li, Yanbo Wang, Shuo Yang, Zhaodong Huang, Qi Yang, Donghong Wang, Binbin Dong, Minshen Zhu, Chunyi Zhi |
---|---|
Format: | Article |
Language: | English |
Published: |
Tsinghua University Press
2022-06-01
|
Series: | Nano Research Energy |
Subjects: | |
Online Access: | https://www.sciopen.com/article/10.26599/NRE.2022.9120002 |
Similar Items
-
Versatile MXenes for Aqueous Zinc Batteries
by: Huan Liu, et al.
Published: (2024-02-01) -
Effect of pinholes in Nb4C3 MXene sheets on its electrochemical behavior in aqueous electrolytes
by: Shuangshuang Zhao, et al.
Published: (2022-09-01) -
Interface Polarization Effects Enhancing Mn2O3@TiO2@MXene Heterostructures for Aqueous Magnesium Ion Capacitors: Guided Charge Distribution and Transportation via Built‐in Electric Fields
by: Mudi Li, et al.
Published: (2024-02-01) -
Capacitors Consisting of an Aqueous Electrolyte of the Widest Potential Window —Development towards the Recovery of Regenerating Energy of Automobiles—
by: Yoon-Yul PARK, et al.
Published: (2020-05-01) -
Fabrication of an Organic Redox Capacitor with a Neutral Aqueous Electrolyte Solution
by: Yuto NAKAGAWA, et al.
Published: (2021-05-01)