| Summary: | Ion irradiation is a promising tool to emulate neutron-irradiation effects on reactor pressure vessel (RPV) steels, especially in the situation of limited availability of suitable neutron-irradiated material. This approach requires the consideration of ion-neutron transferability issues, which are addressed in the present study by comparing the effect of ions with neutron-irradiation effects reported for the same materials. The first part of the study covers a comprehensive characterization, based on dedicated electron microscopy techniques, of the selected unirradiated RPV materials, namely a base metal and a weld. The results obtained for the grain size, dislocation density, and precipitates are put in context in terms of hardening contributions and sink strength. The second part is focused on the depth-dependent characterization of the dislocation loops formed in ion-irradiated samples. This work is based on scanning transmission electron microscopy applied to cross-sectional samples prepared by the focused ion beam technique. A band-like arrangement of loops is observed in the depth range close to the peak of injected interstitials. Two levels of displacement damage, 0.1 and 1 dpa (displacements per atom), as well as post-irradiation annealed conditions, are included for both RPV materials. Compared with neutron irradiation, ion irradiation creates a similar average size but a higher number density of loops presumably due to the higher dose rate during ion irradiation.
|
|---|