Microstructural Evolution, Thermodynamics, and Kinetics of Mo-Tm2O3 Powder Mixtures during Ball Milling
The microstructural evolution, thermodynamics, and kinetics of Mo (21 wt %) Tm2O3 powder mixtures during ball milling were investigated using X-ray diffraction and transmission electron microscopy. Ball milling induced Tm2O3 to be decomposed and then dissolved into Mo crystal. After 96 h of ball mil...
Main Authors: | Yong Luo, Guang Ran, Nanjun Chen, Qiang Shen, Yaoli Zhang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2016-10-01
|
Series: | Materials |
Subjects: | |
Online Access: | http://www.mdpi.com/1996-1944/9/10/834 |
Similar Items
-
The Influence of Powder Milling on Properties of SPS Compacted FeAl
by: Alena Michalcová, et al.
Published: (2020-05-01) -
Synthesis and Characterization of Graphene sheets from graphite powder by using ball milling
by: Zahoor Awan, et al.
Published: (2022-07-01) -
Effect of Ball-Milling Process on Microwave Absorption Behaviors of Flaky Carbonyl Iron Powders
by: Siyuan Yang, et al.
Published: (2023-06-01) -
Microstructure and magnetic properties of MnBi powders prepared by various ball milling processes
by: Chengyu Li, et al.
Published: (2024-01-01) -
Continuous and Intermittent Planetary Ball Milling Effects on the Alloying of a Bismuth Antimony Telluride Powder Mixture
by: Georgios Samourgkanidis, et al.
Published: (2023-05-01)