Polymerization of D,L-lactide in the presence of Boltorn™ polyester polyol
Objects. To synthesize monodisperse biodegradable hyperbranched polymers based on D,L-lactide in the presence of Boltorn™ H30 polyester polyol as a macroinitiator.Methods. 1H and 13C nuclear magnetic resonance (NMR) spectroscopy was used to study the chemical structure of the Boltorn™ H30 polyester...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | Russian |
| Published: |
MIREA - Russian Technological University
2022-07-01
|
| Series: | Тонкие химические технологии |
| Subjects: | |
| Online Access: | https://www.finechem-mirea.ru/jour/article/view/1840 |
| Summary: | Objects. To synthesize monodisperse biodegradable hyperbranched polymers based on D,L-lactide in the presence of Boltorn™ H30 polyester polyol as a macroinitiator.Methods. 1H and 13C nuclear magnetic resonance (NMR) spectroscopy was used to study the chemical structure of the Boltorn™ H30 polyester polyol and (Boltorn™ H30)-PDLA hyperbranched copolymers. The molecular weight distribution of the polymers was studied by gel permeation chromatography (GPC). In order to study the thermal stability of Boltorn™ H30 polyester polyol, thermogravimetric analysis (TGA) was used. Polymerization of D,L-lactide was carried out in a block in the presence of Boltorn™ H30 polyester polyol.Results. The degree of branching of Boltorn™ H30 polyester polyol was calculated from NMR data, while the TGA method was used to determine the upper operational temperature range. The polymerization of D,L-lactide in the presence of Boltorn™ H30 polyester polyol used as a macroinitiator was studied. The molecular weight characteristics of the obtained copolymers were studied by NMR and GPC.Conclusions. Optimum conditions were determined for the polymerization of D,L-lactide when using Boltorn™ H30 polyester polyol as a macroinitiator. The possibility of synthesizing narrowly dispersed hyperbranched polymers (Boltorn™ H30)-PDLA under the described conditions was demonstrated. |
|---|---|
| ISSN: | 2410-6593 2686-7575 |