Structure Analysis and Its Correlation with Mechanical Properties of Microcellular Polyamide Composites Reinforced with Glass Fibers
Thin-walled and thick-walled microcellular moldings were obtained by MuCell<sup>®</sup> technology with nitrogen as a supercritical fluid. 2 mm thick polyamide 6 (PA6) with 30% wt. glass fiber (GF) samples were cut from automotive industrial elements, while 4 mm, 6 mm, and 8.4 mm thick m...
Main Authors: | Piotr Szewczykowski, Dariusz Sykutera, Piotr Czyżewski, Mieczysław Cieszko, Zbigniew Szczepański, Bartosz Nowinka |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-12-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/16/23/7501 |
Similar Items
-
High-Performance of a Thick-Walled Polyamide Composite Produced by Microcellular Injection Molding
by: Dariusz Sykutera, et al.
Published: (2021-07-01) -
The Microcellular Structure of Injection Molded Thick-Walled Parts as Observed by In-Line Monitoring
by: Dariusz Sykutera, et al.
Published: (2020-11-01) -
In Situ Wettability Investigation of Aging of Sandstone Surface in Alkane via X-ray Microtomography
by: Nilesh Kumar Jha, et al.
Published: (2020-10-01) -
Mechanical properties of ABS samples manufactured under different process conditions
by: Piotr Czyżewski, et al.
Published: (2023-12-01) -
Analysis of pore geometry in the compacted fine aggregate matrix by x-ray microtomography
by: Rogério Ferreira Costa
Published: (2022-12-01)