Diffusion Bonding and Post-Weld Heat Treatment of Extruded AZ91 Magnesium Alloys
<span><p>The grain size of as-extruded AZ91 magnesium alloys was refined to 12.31 μm from 21.41 μm by recrystallization annealing. The vacuum diffusion welding of as-annealed AZ91 magnesium alloys was researched. The results showed that the maximum shear strength of joints reached 64.70 ...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Kaunas University of Technology
2015-11-01
|
| Series: | Medžiagotyra |
| Subjects: | |
| Online Access: | http://matsc.ktu.lt/index.php/MatSc/article/view/9699 |
| Summary: | <span><p>The grain size of as-extruded AZ91 magnesium alloys was refined to 12.31 μm from 21.41 μm by recrystallization annealing. The vacuum diffusion welding of as-annealed AZ91 magnesium alloys was researched. The results showed that the maximum shear strength of joints reached 64.70 MPa in the situation of 10 MPa bonding pressure, 18 Pa vacuum degree, 470 °C bonding temperature and 90 min bonding time; both bonding temperature and time are the main influence factors on as-extruded AZ91 magnesium alloys diffusion welding. Then the diffusion welded specimens were annealed, and the shear strength of joints was further improved to 76.93 MPa.</p></span><p>DOI: <a href="http://dx.doi.org/10.5755/j01.ms.21.4.9699">http://dx.doi.org/10.5755/j01.ms.21.4.9699</a></p> |
|---|---|
| ISSN: | 1392-1320 2029-7289 |