Investigation of Stress Corrosion Cracking in Magnesium Alloys by Quantitative Fractography Methods
The article shows that the use of quantitative fracture description may lead to significant progress in research on the phenomenon of stress corrosion cracking of the WE43 magnesium alloy. Tests were carried out on samples in air, and after hydrogenation in 0.1 M Na2SO4 with cathodic polarization. F...