| Summary: | Polyimide (PI) aerogels were prepared using self-designed silicone polymer cross-linkers with multi-amino from low-cost silane coupling agents to replace conventional small-molecule cross-linkers. The long-chain structure of silicone polymers provides more crosslinking points than small-molecule cross-linkers, thus improving the mechanical properties of polyimide. To investigate the effects of amino content and degree of polymerization on the properties of silicone polymers, the different silicone polymers and their cross-linked PI aerogels were prepared. The obtained PI aerogels exhibit densities as low as 0.106 g/cm<sup>3</sup> and specific surface areas as high as 314 m<sup>2</sup>/g, and the maximum Young’s modulus of aerogel is up to 20.9 MPa when using (T-20) as cross-linkers. The cross-linkers were an alternative to expensive small molecule cross-linkers, which can improve the mechanical properties and reduce the cost of PI aerogels.
|
|---|