| Summary: | The liquid phase separation (LPS) behavior in Co-Cr-based high-entropy alloys (HEAs) is an important target for the development of Co-Cr-based HEAs for metallic biomaterials (BioHEAs). The solidification microstructure in Ag-Co-Cr-Fe-Mn-Ni-Ag, Co-Cr-Cu-Fe-Mn-Ni-Cu, and Co-Cr-Cu-Fe-Mn-Ni-B HEAs, which were designed as the combination of the equiatomic CoCrFeMnNi with Ag, Cu, and the interstitial element of B, was investigated as the fundamental research of LPS in Co-Cr-based HEAs. Ingots of equiatomic AgCoCrFeMnNi, equiatomic CoCrCuFeMnNi, non-equiatomic CoCrCu<sub>x</sub>FeMnNi (x = 2, 3), and CoCrCu<sub>x</sub>FeMnNiB<sub>0.2</sub> (x = 1, 2, 3) with a small amount of B were fabricated using the arc-melting process. A macroscopic phase-separated structure was observed in the ingots of the equiatomic AgCoCrFeMnNi and CoCrCu<sub>x</sub>FeMnNiB<sub>0.2</sub> (x = 2, 3) HEAs. The addition of a small amount of B enhanced the LPS tendency in the Co-Cr-Fe-Mn-Ni-Cu HEAs. The LPS behavior was discussed through the heat of mixing and computer coupling of phase diagrams and thermochemistry (CALPHAD).
|
|---|