| Summary: | While an anodizing process is essential for magnesium alloys to be used under corrosive environments, it sometimes stimulates a fatigue fracture that initiates at the interface between the coating layer and the substrate. In this study, a plasma electrolyte oxidation (PEO) technique was employed to provide excellent adhesion between the anodizing layer and the AM50 die-cast by applying an extremely high dielectric discharge in an alkaline phosphate electrolyte, and its effect on corrosion and fatigue behaviors was investigated. The stress intensity factor at the fatigue limit was estimated to be 0.28 MPam<sup>0.5</sup>. The specimen anodized using the PEO technique exhibits enhanced strength and corrosion resistance compared to the unanodized counterpart. Furthermore, it shows a relative fatigue life in spite of the thick anodizing layer because the crack initiates from the interface, not from the pore near the interface.
|
|---|