HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI

<p><strong>CELLULOCE HYDROLYSIS TO GLUCOSE USING ACTIVE CARBON SULPHONATED HETEROGENOUS CATALYST. </strong><em>Enzimatic process and acid hydrolysis process are common process for conversion of cellulose to glucose. Unfornately, the two processes are expensive process and kor...

Full description

Bibliographic Details
Main Authors:	Didi Dwi Anggoro, Purwanto Purwanto, Rispiandi Rispiandi
Format:	Article
Language:	English
Published:	Diponegoro University 2014-12-01
Series:	Reaktor
Subjects:	Selulosa, glukosa, alang-alang, karbon aktif tersulfonasi
Online Access:	http://ejournal.undip.ac.id/index.php/reaktor/article/view/8394

_version_	1818601802648518656
author	Didi Dwi Anggoro Purwanto Purwanto Rispiandi Rispiandi
author_facet	Didi Dwi Anggoro Purwanto Purwanto Rispiandi Rispiandi
author_sort	Didi Dwi Anggoro
collection	DOAJ
description	<p><strong>CELLULOCE HYDROLYSIS TO GLUCOSE USING ACTIVE CARBON SULPHONATED HETEROGENOUS CATALYST. </strong><em>Enzimatic process and acid hydrolysis process are common process for conversion of cellulose to glucose. Unfornately, the two processes are expensive process and korosif process. Hence, the new process, that use sulfonaned active carbon catalyst is important to developing. The sulfonated active carbon is made from carbonated coconut sheel under temperature at 350<sup>o</sup>C. After carbonation, sulfonated active carbon soaked under sulphate acid 96% at 150<sup>o</sup>C until 15 hours. </em><em>The result is then</em><em> washed and dried, and tested catalyst characteristics in the form of H<sup>+</sup> capacity, pore size catalysts by used BET surface area, functional groups by used FTIR, and morphology catalyst structure by used SEM. Catalyst performance was tested in an autoclave reactor through a hydrothermal process with difference of the catalyst amount and temperature. The results showed that the test characteristics of H<sup>+</sup> capacity is 2.95 mmol/g, the pore size is 29 m2/gr. FTIR analyze showed that the presence of sulfonate groups read at a wavelength of vibration 1750 cm<sup>-1</sup> and 1379 cm<sup>-1</sup>. By SEM analyze showed that the morphological structure of sulfonated active carbon is more open than other catalyst. By testing catalyst, the highest conversion of glucose is 87.2 %.</em><em> </em></p> <p><strong> </strong></p> <p><strong>Keywords: </strong><em>cellulose</em><em>;</em><em> glucose</em><em>;</em><em> </em><em>sulfonate active carbon</em><em>;</em><em> </em><em>thatch</em></p> <p><strong> </strong></p> <p><strong> </strong></p> <p><strong>Abstrak</strong></p> <p><strong> </strong></p> <p><em>Teknologi yang sudah digunakan dalam mengubah selulosa menjadi glukosa adalah dengan proses enzimatik dan hidrolisis asam. Kedua teknologi tersebut masih memiliki kendala teknis, yaitu harga enzim yang mahal, proses yang korosif dan menimbulkan limbah, sehingga diperlukan pengembangan teknologi baru salah satu diantaranya yaitu dengan metode katalis heterogen berupa karbon aktif tersulfonasi. Karbon aktif tersulfonasi ini dibuat dari tempurung kelapa yang dikarbonisasi pada temperatur 350<sup>o</sup>C, selanjutnya direndam dalam asam sulfat 96% pada temperatur 150<sup>o</sup>C selama 15 jam. Hasilnya kemudian dicuci dan dikeringkan, dilakukan uji karakteristik dan performance (kinerja ) katalis berupa kapasitas H<sup>+</sup>, ukuran pori katalis dengan BET, uji gugus fungsi dengan FTIR, dan uji struktur marfologi katalis dengan SEM. Kinerja katalis diuji dalam reaktor autoclave melalui proses hidrotermal dengan mevariasikan jumlah katalis, dan variasi temperatur. Hasil penelitian menunjukkan untuk uji karakteristik kapasitas H<sup>+</sup> sebesar 2</em><em>,</em><em>95 mmol/gr, untuk uji BET ukuran pori 29 m<sup>2</sup>/gr , untuk uji FTIR keberadaan gugus sulfonat terbaca pada vibrasi panjang gelombang 1750 cm<sup>-1</sup> dan 1379 cm<sup>-1</sup> , pada uji SEM struktur morfologi katalis yang lebih terbuka pada karbon aktif setelah proses sulfonasi. Kinerja katalis konversi tertinggi selulosa menjadi glukosa mencapai 87,2% pada jumlah alang-alang 2 gr, jumlah katalis 2 gr, dan temperatur 170<sup>o</sup>C selama 8 jam.</em><em> </em></p> <p><strong> </strong></p> <p><strong>Kata kunci :</strong><em> s</em><em>elulosa</em><em>;</em><em> glukosa</em><em>;</em><em> </em><em>karbon aktif tersulfonasi; alang-alang</em></p><br />
first_indexed	2024-12-16T12:57:10Z
format	Article
id	doaj.art-2491ccffa84d4f88b92ffdd3636eea37
institution	Directory Open Access Journal
issn	0852-0798 2407-5973
language	English
last_indexed	2024-12-16T12:57:10Z
publishDate	2014-12-01
publisher	Diponegoro University
record_format	Article
series	Reaktor
spelling	doaj.art-2491ccffa84d4f88b92ffdd3636eea372022-12-21T22:30:58ZengDiponegoro UniversityReaktor0852-07982407-59732014-12-0115212613110.14710/reaktor.15.2.126-1317305HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASIDidi Dwi Anggoro0Purwanto Purwanto1Rispiandi Rispiandi2Diponegoro UniversityDiponegoro UniversityPoliteknik Bandung<p><strong>CELLULOCE HYDROLYSIS TO GLUCOSE USING ACTIVE CARBON SULPHONATED HETEROGENOUS CATALYST. </strong><em>Enzimatic process and acid hydrolysis process are common process for conversion of cellulose to glucose. Unfornately, the two processes are expensive process and korosif process. Hence, the new process, that use sulfonaned active carbon catalyst is important to developing. The sulfonated active carbon is made from carbonated coconut sheel under temperature at 350<sup>o</sup>C. After carbonation, sulfonated active carbon soaked under sulphate acid 96% at 150<sup>o</sup>C until 15 hours. </em><em>The result is then</em><em> washed and dried, and tested catalyst characteristics in the form of H<sup>+</sup> capacity, pore size catalysts by used BET surface area, functional groups by used FTIR, and morphology catalyst structure by used SEM. Catalyst performance was tested in an autoclave reactor through a hydrothermal process with difference of the catalyst amount and temperature. The results showed that the test characteristics of H<sup>+</sup> capacity is 2.95 mmol/g, the pore size is 29 m2/gr. FTIR analyze showed that the presence of sulfonate groups read at a wavelength of vibration 1750 cm<sup>-1</sup> and 1379 cm<sup>-1</sup>. By SEM analyze showed that the morphological structure of sulfonated active carbon is more open than other catalyst. By testing catalyst, the highest conversion of glucose is 87.2 %.</em><em> </em></p> <p><strong> </strong></p> <p><strong>Keywords: </strong><em>cellulose</em><em>;</em><em> glucose</em><em>;</em><em> </em><em>sulfonate active carbon</em><em>;</em><em> </em><em>thatch</em></p> <p><strong> </strong></p> <p><strong> </strong></p> <p><strong>Abstrak</strong></p> <p><strong> </strong></p> <p><em>Teknologi yang sudah digunakan dalam mengubah selulosa menjadi glukosa adalah dengan proses enzimatik dan hidrolisis asam. Kedua teknologi tersebut masih memiliki kendala teknis, yaitu harga enzim yang mahal, proses yang korosif dan menimbulkan limbah, sehingga diperlukan pengembangan teknologi baru salah satu diantaranya yaitu dengan metode katalis heterogen berupa karbon aktif tersulfonasi. Karbon aktif tersulfonasi ini dibuat dari tempurung kelapa yang dikarbonisasi pada temperatur 350<sup>o</sup>C, selanjutnya direndam dalam asam sulfat 96% pada temperatur 150<sup>o</sup>C selama 15 jam. Hasilnya kemudian dicuci dan dikeringkan, dilakukan uji karakteristik dan performance (kinerja ) katalis berupa kapasitas H<sup>+</sup>, ukuran pori katalis dengan BET, uji gugus fungsi dengan FTIR, dan uji struktur marfologi katalis dengan SEM. Kinerja katalis diuji dalam reaktor autoclave melalui proses hidrotermal dengan mevariasikan jumlah katalis, dan variasi temperatur. Hasil penelitian menunjukkan untuk uji karakteristik kapasitas H<sup>+</sup> sebesar 2</em><em>,</em><em>95 mmol/gr, untuk uji BET ukuran pori 29 m<sup>2</sup>/gr , untuk uji FTIR keberadaan gugus sulfonat terbaca pada vibrasi panjang gelombang 1750 cm<sup>-1</sup> dan 1379 cm<sup>-1</sup> , pada uji SEM struktur morfologi katalis yang lebih terbuka pada karbon aktif setelah proses sulfonasi. Kinerja katalis konversi tertinggi selulosa menjadi glukosa mencapai 87,2% pada jumlah alang-alang 2 gr, jumlah katalis 2 gr, dan temperatur 170<sup>o</sup>C selama 8 jam.</em><em> </em></p> <p><strong> </strong></p> <p><strong>Kata kunci :</strong><em> s</em><em>elulosa</em><em>;</em><em> glukosa</em><em>;</em><em> </em><em>karbon aktif tersulfonasi; alang-alang</em></p><br />http://ejournal.undip.ac.id/index.php/reaktor/article/view/8394Selulosa, glukosa, alang-alang, karbon aktif tersulfonasi
spellingShingle	Didi Dwi Anggoro Purwanto Purwanto Rispiandi Rispiandi HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI Reaktor Selulosa, glukosa, alang-alang, karbon aktif tersulfonasi
title	HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI
title_full	HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI
title_fullStr	HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI
title_full_unstemmed	HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI
title_short	HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI
title_sort	hidrolisis selulosa menjadi glukosa dengan katalis heterogen arang aktif tersulfonasi
topic	Selulosa, glukosa, alang-alang, karbon aktif tersulfonasi
url	http://ejournal.undip.ac.id/index.php/reaktor/article/view/8394
work_keys_str_mv	AT dididwianggoro hidrolisisselulosamenjadiglukosadengankatalisheterogenarangaktiftersulfonasi AT purwantopurwanto hidrolisisselulosamenjadiglukosadengankatalisheterogenarangaktiftersulfonasi AT rispiandirispiandi hidrolisisselulosamenjadiglukosadengankatalisheterogenarangaktiftersulfonasi

HIDROLISIS SELULOSA MENJADI GLUKOSA DENGAN KATALIS HETEROGEN ARANG AKTIF TERSULFONASI

Similar Items