Microstructure and ablation properties of C/C-Zr-Si-O composites prepared by carbothermal reduction of hydrothermal co-deposited oxides
C/C-Zr-Si-O composites were prepared by carbothermal reduction of hydrothermal co-deposited ZrO2, SiO2, and C. The bulk density of composites reached 1.71 g/cm3 with 8 cycles of co-deposition. The matrix of the composites includes ZrC, SiC, ZrO2, and SiO2 with fine grain size (300–500 nm) and homoge...
Main Authors: | Haibo Ouyang, Guibiao Li, Cuiyan Li, Jianfeng Huang, Jie Fei, Jing Lu |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2018-12-01
|
Series: | Materials & Design |
Online Access: | http://www.sciencedirect.com/science/article/pii/S0264127518306683 |
Similar Items
-
Microstructure and properties of C/C-CuNi composites fabricated by carbothermal reduction of hydrothermal co-deposited oxides
by: Haibo Ouyang, et al.
Published: (2022-09-01) -
Fabrication of ZrC/SiC, ZrO2/SiC and ZrO2 powders by carbothermal reduction of ZrSiO4
by: Ljiljana Kljajević, et al.
Published: (2011-06-01) -
SYNTHESIS AND MECHANISM OF SiC-ZrC COMPOSITE POWDERS BY CARBOTHERMAL REDUCTION METHOD
by: Yu Cao, et al.
Published: (2022-10-01) -
ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites
by: Cuiyan Li, et al.
Published: (2019-03-01) -
Investigation of the properties of ZrC nanopowder synthesized by the carbothermal reduction method using phenolic resin
by: Farhad Farhang Rad, et al.
Published: (2024-03-01)