Activating Flux TIG Welding Technology of 2219 High Strength Aluminum Alloy
Straight polarity direct current method(DCSP A-TIG) was applied to join 2219 high strength aluminum alloy, and the effects of single-component(AlF<sub>3</sub>,LiF), three-component (AlF<sub>3</sub>+30%LiF+10%KF-AlF<sub>3</sub>) and four-component (AlF<sub>3&...
Main Authors: | LI Hui, ZOU Jia-sheng, YAO Jun-shan, PENG Hao-ping |
---|---|
Format: | Article |
Language: | zho |
Published: |
Journal of Materials Engineering
2018-04-01
|
Series: | Cailiao gongcheng |
Subjects: | |
Online Access: | http://jam.biam.ac.cn/CN/Y2018/V46/I4/66 |
Similar Items
-
Study on Residual Stresses of 2219 Aluminum Alloy with TIG Welding and Its Reduction by Shot Peening
by: Tao Zhang, et al.
Published: (2023-09-01) -
Improving the Formation and Quality of Weld Joints on Aluminium Alloys during TIG Welding Using Flux Backing Tape
by: Saidov Rustam Mannapovich, et al.
Published: (2024-03-01) -
Effect of Shot Peening on Redistribution of Residual Stress Field in Friction Stir Welding of 2219 Aluminum Alloy
by: Lin Nie, et al.
Published: (2020-07-01) -
Study on the Properties of a 2219 Aluminum Alloy Friction Stir-Welded Joint under the Biaxial Stress State
by: Minghao Shao, et al.
Published: (2023-11-01) -
Investigation on welding defects of alloys using TIG and MIG welding
by: Syed Rashedul Haque
Published: (2023-08-01)