Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024
Through investigating the effect of parameters on the fatigue properties and crack propagation behavior of friction stir crack repaired 2024 aluminum alloy, we demonstrated that the fatigue strength of friction stir repaired Al2024 was sensitive to the repairing parameters and had a “V” type discipl...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2020-07-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2075-4701/10/8/1026 |
| _version_ | 1797560667741356032 |
|---|---|
| author | Lei Wang Jiahui Cong Jungang Ren Li Hui Song Zhou |
| author_facet | Lei Wang Jiahui Cong Jungang Ren Li Hui Song Zhou |
| author_sort | Lei Wang |
| collection | DOAJ |
| description | Through investigating the effect of parameters on the fatigue properties and crack propagation behavior of friction stir crack repaired 2024 aluminum alloy, we demonstrated that the fatigue strength of friction stir repaired Al2024 was sensitive to the repairing parameters and had a “V” type discipline with the rotating speed or advancing velocity. The fatigue crack growth rates of the repaired specimens were higher than the base material counterpart, and the crack propagation mechanism in the repaired zone was mainly intergranular. When the improper repairing parameters were adopted, the delamination defect would form at the interfaces between the repaired layer and base material |
| first_indexed | 2024-03-10T18:02:53Z |
| format | Article |
| id | doaj.art-2634ee70794d49b7b9654f907b73ed1f |
| institution | Directory Open Access Journal |
| issn | 2075-4701 |
| language | English |
| last_indexed | 2024-03-10T18:02:53Z |
| publishDate | 2020-07-01 |
| publisher | MDPI AG |
| record_format | Article |
| series | Metals |
| spelling | doaj.art-2634ee70794d49b7b9654f907b73ed1f2023-11-20T08:40:24ZengMDPI AGMetals2075-47012020-07-01108102610.3390/met10081026Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024Lei Wang0Jiahui Cong1Jungang Ren2Li Hui3Song Zhou4Key Laboratory of Fundamental Science for National Defense of Aeronautical Digital Manufacturing Process, Shenyang Aerospace University, Shenyang 110136, ChinaKey Laboratory of Fundamental Science for National Defense of Aeronautical Digital Manufacturing Process, Shenyang Aerospace University, Shenyang 110136, ChinaDepartment of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004, ChinaKey Laboratory of Fundamental Science for National Defense of Aeronautical Digital Manufacturing Process, Shenyang Aerospace University, Shenyang 110136, ChinaKey Laboratory of Fundamental Science for National Defense of Aeronautical Digital Manufacturing Process, Shenyang Aerospace University, Shenyang 110136, ChinaThrough investigating the effect of parameters on the fatigue properties and crack propagation behavior of friction stir crack repaired 2024 aluminum alloy, we demonstrated that the fatigue strength of friction stir repaired Al2024 was sensitive to the repairing parameters and had a “V” type discipline with the rotating speed or advancing velocity. The fatigue crack growth rates of the repaired specimens were higher than the base material counterpart, and the crack propagation mechanism in the repaired zone was mainly intergranular. When the improper repairing parameters were adopted, the delamination defect would form at the interfaces between the repaired layer and base materialhttps://www.mdpi.com/2075-4701/10/8/1026friction stir crack repairingaluminum alloyfatigue propertycrack propagation |
| spellingShingle | Lei Wang Jiahui Cong Jungang Ren Li Hui Song Zhou Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024 Metals friction stir crack repairing aluminum alloy fatigue property crack propagation |
| title | Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024 |
| title_full | Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024 |
| title_fullStr | Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024 |
| title_full_unstemmed | Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024 |
| title_short | Effect of Parameters on Fatigue Properties and Crack Propagation Behavior of Friction Stir Crack Repaired Al2024 |
| title_sort | effect of parameters on fatigue properties and crack propagation behavior of friction stir crack repaired al2024 |
| topic | friction stir crack repairing aluminum alloy fatigue property crack propagation |
| url | https://www.mdpi.com/2075-4701/10/8/1026 |
| work_keys_str_mv | AT leiwang effectofparametersonfatiguepropertiesandcrackpropagationbehavioroffrictionstircrackrepairedal2024 AT jiahuicong effectofparametersonfatiguepropertiesandcrackpropagationbehavioroffrictionstircrackrepairedal2024 AT jungangren effectofparametersonfatiguepropertiesandcrackpropagationbehavioroffrictionstircrackrepairedal2024 AT lihui effectofparametersonfatiguepropertiesandcrackpropagationbehavioroffrictionstircrackrepairedal2024 AT songzhou effectofparametersonfatiguepropertiesandcrackpropagationbehavioroffrictionstircrackrepairedal2024 |