Geometrical and electrical properties of NTC polycrystalline thermistors vs. Changes of sintering parameters
NTC thermistor powder was made of a Mn, Ni, Fe and Co oxide mixture calcinated at 1050°C / 60 min. The powder was milled in a ball mill down to an average particle diameter of 0.9 μm. Small disc shaped pills of the powder obtained were made by pressing with a pressure of 2.5 MPa. The pills were sint...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
International Institute for the Science of Sintering, Beograd
2006-01-01
|
| Series: | Science of Sintering |
| Subjects: | |
| Online Access: | http://www.doiserbia.nb.rs/img/doi/0350-820X/2006/0350-820X0603223S.pdf |
| Summary: | NTC thermistor powder was made of a Mn, Ni, Fe and Co oxide mixture calcinated at 1050°C / 60 min. The powder was milled in a ball mill down to an average particle diameter of 0.9 μm. Small disc shaped pills of the powder obtained were made by pressing with a pressure of 2.5 MPa. The pills were sintered in the temperature range of 900-1400 °C for 30-240 min. The volume and specific volume resistivity change were measured as a function of sintering conditions. Microstructure development was observed using a SEM microscope. Using the results obtained, optimization of sintering parameters was performed in order to determine optimal electrical properties of the selected thermistor composition. |
|---|---|
| ISSN: | 0350-820X |