Structure and Mechanical Properties of Ti-Al-Ta-N Coatings Deposited by Direct Current and Middle-Frequency Magnetron Sputtering
Ti-Al-Ta-N coatings are characterized by attractive mechanical properties, thermal stability and oxidation resistance, which are superior to ternary compositions, such as Ti-Al-N. However, because of their open columnar microstructure, the Ti-Al-Ta-N coatings deposited by conventional direct current...
Main Authors: | Artur R. Shugurov, Evgenii D. Kuzminov, Yuriy A. Garanin |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-03-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/13/3/512 |
Similar Items
-
The effect of S/Mo ratio on structure and properties of MoSx-Ti composite coatings deposited by magnetron sputtering
by: Tao Wang, et al.
Published: (2020-01-01) -
Taguchi optimization of hardness and scratch adhesion strength of multilayer Ti/TiN coatings on Ti- 51 at%Ni alloy deposited via magnetron sputtering technique
by: Ishiaka Shaibu Arudi, et al.
Published: (2023-11-01) -
Tribocorrosion behaviors of TiSiCN nanocomposite coatings deposited by high power impulse magnetron sputtering
by: Haoqi Wang, et al.
Published: (2020-01-01) -
Comparison of CrN Coatings Prepared Using High-Power Impulse Magnetron Sputtering and Direct Current Magnetron Sputtering
by: Heda Bai, et al.
Published: (2023-09-01) -
Structure, mechanical properties and oxidation resistance of iso and non-iso architected TiN/Cr multilayers coatings deposited by magnetron sputtering
by: Vagner F. G. Soares, et al.
Published: (2021-01-01)