Accelerated Spheroidization of Cementite in Sintered Ultrahigh Carbon Steel by Warm Deformation
Evolution of microstructure and hardness in quenched ultrahigh carbon steel Fe-0.85Mo-0.6Si-1.4C by warm compression on a Bähr plastometer-dilatometer at 775 °C and at 0.001 to 1 s<sup>−1</sup> strain rate range is reported. The material was prepared via powder metallurgy: cold pressing...
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-02-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/11/2/328 |