Mn-Ce Catalysts/LDPC Modified by Mo for Improving NH<sub>3</sub>-SCR Performance and SO<sub>2</sub> Resistance at Low Temperature
Mn-Ce catalysts modified by Mo were loaded on low-density porous ceramics (LDPC) for simultaneous denitrification and dust removal. The Mn-Ce-Mo catalyst on LDPC had nearly 99% NO<sub>x</sub> conversion efficiency from 120 °C to 200 °C and still maintained more than 90% NO<sub>x<...
Main Authors: | Tao Zhou, Jiang Jin, Hua Zhang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-05-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/13/5/938 |
Similar Items
-
Protection Effect of Ammonia on CeNbTi NH<sub>3</sub>-SCR Catalyst from SO<sub>2</sub> Poisoning
by: Yang Gao, et al.
Published: (2022-11-01) -
Research Progress of the Selective Catalytic Reduction with NH<sub>3</sub> over ZSM-5 Zeolite Catalysts for NO<sub>x</sub> Removal
by: Wangxiang Pan, et al.
Published: (2023-10-01) -
Study of the NH<sub>3</sub>-SCR Mechanism on LaMnO<sub>3</sub> Surfaces Based on the DFT Method
by: Dongdong Ren, et al.
Published: (2022-11-01) -
The Latest Research Progress of NH<sub>3</sub>-SCR in the SO<sub>2</sub> Resistance of the Catalyst in Low Temperatures for Selective Catalytic Reduction of NO<sub>x</sub>
by: Caixia Liu, et al.
Published: (2020-09-01) -
Effect of Different Zinc Species on Mn-Ce/CuX Catalyst for Low-Temperature NH<sub>3</sub>-SCR Reaction: Comparison of ZnCl<sub>2</sub>, Zn(NO<sub>3</sub>)<sub>2</sub>, ZnSO<sub>4</sub> and ZnCO<sub>3</sub>
by: Lin Chen, et al.
Published: (2023-08-01)