Microstructural evolution during austempering of a ASTM A-532 CLASS III type high chromium white cast iron undergoing abrasive wear
This paper studies the influence of variables such as holding temperatures and times during austempering of High Chromium White Cast Iron (HCWCI), with the following chemical composition: Cr 25 %, C 3 %, Si 0.47 %, Mn 0.74 % and Mo 1.02 %. The aim of the austempering was to modify the percentage of...
Main Authors: | Oscar Fabián Higuera-Cobos, Jeison Bucurú-Vasco, Andrés Felipe Loaiza-Patiño, Mónica Johanna Monsalve-Arias, Dairo Hernán Mesa-Grajales |
---|---|
Format: | Article |
Language: | English |
Published: |
Universidad Pedagógica y Tecnológica de Colombia
2017-09-01
|
Series: | Revista Facultad de Ingeniería |
Subjects: | |
Online Access: | http://revistas.uptc.edu.co/index.php/ingenieria/article/view/7319 |
Similar Items
-
An Analysis of the Amount of Retained Austenite in Manganese Alloyed Austempered Ductile Iron
by: Sathyashankara Sharma, et al.
Published: (2021-09-01) -
Effect of Different Austempering Heat Treatments on Corrosion Properties of High Silicon Steel
by: Mattia Franceschi, et al.
Published: (2021-01-01) -
Machinability and related properties of austempered ductile iron: A review
by: Ananda Hegde, et al.
Published: (2018-12-01) -
Effect of Intercritical Annealing and Austempering on the Microstructure and Mechanical Properties of a High Silicon Manganese Steel
by: Mattia Franceschi, et al.
Published: (2020-10-01) -
Wear resistance of austempered grey iron under dry and wet conditions
by: Carlos Humberto Navarro-Mesa, et al.
Published: (2022-11-01)