Abrasive Wear of High-Carbon Low-Alloyed Austenite Steel: Microhardness, Microstructure and X-ray Characteristics of Worn Surface
A high-carbon, high-silicon steel (1.21 wt% C, 2.56 wt% Mn, 1.59 wt% Si) was subjected to quenching from 900 and 1000 °C, resulting in microstructures containing 60 and 94% of retained austenite, respectively. Subsequent abrasive wear tests of quenched samples were performed using two-body abrasion...
Main Authors: | Michail Nikolaevich Brykov, Taisiia Oleksandrivna Akrytova, Michail Jurievich Osipov, Ivan Petryshynets, Viktor Puchy, Vasily Georgievich Efremenko, Kazumichi Shimizu, Maik Kunert, Olaf Hesse |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-10-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/14/20/6159 |
Similar Items
-
Fall Detection With Wrist-Worn Watch by Observations in Statistics of Acceleration
by: Songsheng Li
Published: (2023-01-01) -
Explain physical resilience in urban worn texture using PLS structural equations(Case study: Neighborhoods of the third region of Isfahan)
by: mahshid gorji, et al.
Published: (2021-09-01) -
Preferable Stability Speed of Metro Vehicles Passing Steel Spring Floating Slab Tracks with Worn Wheels
by: Jinming ZHANG, et al.
Published: (2024-01-01) -
Rehabilitation of a Severely Worn Dentition with Partial Lithium-Disilicate Glass Ceramic Restorations: A Case Report
by: Ece İrem Oğuz, et al.
Published: (2021-04-01) -
Significance Analysis - The performance of key success factors in regenerating worn-out urban(Case study: Zanjan city)
by: Mohammad Rasoli, et al.
Published: (2021-05-01)