Local Fatigue Strength Evaluation of Shot Peened 40Cr Notched Steel
Fatigue life prediction for the notched components is an essential step within the design process of machines. Fatigue strength and life prediction of 40Cr notched steel before and after shot peening were studied. Fatigue fracture of specimens treated by three shot peening intensity parameters was d...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2018-08-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | http://www.mdpi.com/2075-4701/8/9/681 |
| Summary: | Fatigue life prediction for the notched components is an essential step within the design process of machines. Fatigue strength and life prediction of 40Cr notched steel before and after shot peening were studied. Fatigue fracture of specimens treated by three shot peening intensity parameters was discussed. The life prediction considering residual stress, work hardening and surface roughness caused by shot peening was analyzed. The results indicated that fatigue strength was obviously improved after shot peening and the improvement effect was gradually enhanced with the increase of shot peening intensity. The predicted values based on Rz coefficient showed a good correspondence with the experimental data. |
|---|---|
| ISSN: | 2075-4701 |