Formation of Al3Ti/Mg composite by powder metallurgy of Mg–Al–Ti system
An in situ titanium trialuminide (Al3Ti)-particle-reinforced magnesium matrix composite has been successfully fabricated by the powder metallurgy of a Mg–Al–Ti system. The reaction processes and formation mechanism for synthesizing the composite were studied by differential scanning calorimetry (DSC...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Taylor & Francis Group
2008-01-01
|
| Series: | Science and Technology of Advanced Materials |
| Subjects: | |
| Online Access: | http://www.iop.org/EJ/abstract/1468-6996/9/3/035005 |
| Summary: | An in situ titanium trialuminide (Al3Ti)-particle-reinforced magnesium matrix composite has been successfully fabricated by the powder metallurgy of a Mg–Al–Ti system. The reaction processes and formation mechanism for synthesizing the composite were studied by differential scanning calorimetry (DSC), x-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS). Al3Ti particles are found to be synthesized in situ in the Mg alloy matrix. During the reaction sintering of the Mg–Al–Ti system, Al3Ti particles are formed through the reaction of liquid Al with as-dissolved Ti around the Ti particles. The formed intermetallic particles accumulate at the original sites of the Ti particles. As sintering time increases, the accumulated intermetallic particles disperse and reach a relatively homogeneous distribution in the matrix. It is found that the reaction process of the Mg–Al–Ti system is almost the same as that of the Al–Ti system. Mg also acts as a catalytic agent and a diluent in the reactions and shifts the reactions of Al and Ti to lower temperatures. An additional amount of Al is required for eliminating residual Ti and solid-solution strengthening of the Mg matrix. |
|---|---|
| ISSN: | 1468-6996 1878-5514 |