| Summary: | This paper studies boron precipitation and segregation at austenitic grain boundaries for low carbon boron steels types: PL22 and 15BCr30. The following parameters were evaluated: percentage of martensite/bainite, size and nucleation sites of austenitic grains and precipitates sizes. Three austenitization temperatures were studied (870, 1050 and 1200 °C). The highest martensite percentage occurred for 1050 °C. Iron-borocarbides were detected at grain boundaries for all tested temperatures. At 870 °C the coarse iron-borocarbides are due to non-solubility and coalescence. The highest martensite percentage at 1050 °C is caused by the discrete precipitation of iron-borocarbides at austenitic grains boundaries. The discrete precipitation was due to the low non-equilibrium segregation of boron at grain boundaries. The low non-equilibrium segregation and the small grain size at 1050 °C reduce the total boron concentration at grain boundaries.
|
|---|