Effects of B on the Segregation Behavior of Mo at the Fe–Cr(111)/Cr<sub>2</sub>O<sub>3</sub>(0001) Interface: A First-Principles Study
The addition of B can inhibit the precipitation of σ phases at the grain boundary to improve the hot workability and corrosion resistance for super austenitic stainless steel with high Cr and Mo content. This study focused on the interaction between B and Mo at the Fe–Cr(111)/Cr<sub>2</sub&...
Main Authors: | Yanlu Zhang, Caili Zhang, Zhuxia Zhang, Nan Dong, Jian Wang, Ying Liu, Zhibo Lei, Peide Han |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-04-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/10/5/577 |
Similar Items
-
First Principle Study of TiB<sub>2</sub> (0001)/γ-Fe (111) Interfacial Strength and Heterogeneous Nucleation
by: Qin Wang, et al.
Published: (2021-03-01) -
First-Principles Study on the Structural Stability and Segregation Behavior of γ-Fe/Cr2N Interface with Alloying Additives M (M = Mn, V, Ti, Mo, and Ni)
by: Hui Huang, et al.
Published: (2016-07-01) -
Interfacial Thermal Conductance across Graphene/MoS<sub>2</sub> van der Waals Heterostructures
by: Shuang Wu, et al.
Published: (2020-11-01) -
Effect of B on Segregation Behavior of Mo at γ-Fe ∑9 and ∑11 Grain Boundaries
by: Xin YAN, et al.
Published: (2023-11-01) -
The Effect of B on the Co-Segregation of C-Cr at Grain Boundaries in Austenitic Steels
by: Xin Yan, et al.
Published: (2023-05-01)